PA/ABS

PA/ABS Terblend®N N NM-11 BASF USA

326

Unit Price:US$ 2,871 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
91MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High mobility｜High impact resistance｜Easy to process
Application Areas:Helmet｜sporting goods｜Automotive sector｜Shell｜Application in the automotive field
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	-30°C	ISO 179	无断裂
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179	无断裂

mechanical properties	Test Condition	Test Method	Test Result
Tensile strain	Yield,23°C	ISO 527-2	3.5 %
Bending modulus		ISO 178	1800 Mpa
bending strength		ISO 178	62.0 Mpa
Tensile modulus		ISO 527-2	2000 Mpa
tensile strength	Yield,23°C	ISO 527-2	43.0 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Annealed	ISO 75-2/B	85.0 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Annealed	ISO 75-2/A	65.0 °C
Vicat softening temperature	--	ISO 306/A50	160 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	102 °C
Linear coefficient of thermal expansion	MD	ISO 11359-2	1E-04 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
Melt Volume Flow Rate (MVR)	240°C/10.0kg	ISO 1133	30.0 cm3/10min
Shrinkage rate		ISO 294-4	0.80 %
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	1.2 %

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		IEC 60093	1E+14 ohms
Volume resistivity		IEC 60093	>1.0E+15 ohms·cm
Relative permittivity	1MHz	IEC 60250	2.90
Dissipation factor	1MHz	IEC 60250	0.015

hardness	Test Condition	Test Method	Test Result
Ball Pressure Test		ISO 2039-1	86.0 Mpa

film	Test Condition	Test Method	Test Result
elongation	Break	ISO 527-3	>50 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PA/ABS Terblend®N N NM-11 BASF USA

Material Description

Technical Data Sheet Compare

Technical Data Sheet