PBT Cristin® SK601 BK851 DUPONT USA
234
- Unit Price:US$ 2,653 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:25MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Glass fiber reinforced
- Application Areas:Automotive Applications｜Electronic and electrical components
- Color:--
- Grade:Enhanced level
Material Certification
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 6.00 mm | UL 94 | HB |
| 3.00 mm | UL 94 | HB | |
| 1.50 mm | UL 94 | HB | |
| Heat Deflection Temperature | 1.8MPa,未退火 | ISO 75-2/A | 180 °C |
| melting temperature | ISO 11357-3 | 225 °C | |
| Combustibility (rate) | UL 94 | HB | |
| Heat Deflection Temperature | HDT | ASTM D648/ISO 75 | 180 ℃（℉） |
| melting temperature | 225 ℃（℉） |
| other | Test Condition | Test Method | Test Result |
|---|---|---|---|
| characteristic | 10%玻纤增强.润滑.注射成型 |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| burning rate | 1.00mm | ISO 3795 | 36 mm/min |
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| 3.0mm | UL 94 | HB | |
| 1.5mm | IEC 60695-11-10,-20 | HB | |
| 3.0mm | IEC 60695-11-10,-20 | HB | |
| Limiting Oxygen Index | ISO 4589-2 | 20 % | |
| FMVSS flammability | FMVSS302 | B | |
| Fogging-G-value | condensate | ISO 6452 | 1E-04 g |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Emissions of Organic Compounds | VDA277 | 72.0 µgC/g | |
| Odor | VDA270 | 3.00 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 35 kJ/m² |
| 23°C | ISO 179/1eU | 35 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 2 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Ejection Temperature | 170 °C | ||
| density | ASTM D792/ISO 1183 | 1370 | |
| shrinkage rate | ASTM D955 | 1.2 % | |
| Water absorption rate | ASTM D570/ISO 62 | 0.2 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | 0.00 mm, 23℃, Injection Molded | ISO 527-1 | 4500 MPa |
| bending strength | 0.00 mm, 23 ℃, 0.0 % | ISO 178 | 140 MPa |
| Tensile modulus | ISO 527-2 | 4500 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 90.0 Mpa |
| Tensile strain | 断裂 | ISO 527-2 | 4.0 % |
| bending strength | ISO 178 | 140 Mpa | |
| Elongation at break | ASTM D638/ISO 527 | 4 % | |
| bending strength | ASTM D790/ISO 178 | 140 kg/cm²(MPa)[Lb/in²] |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.