PA6

PA6 Zytel® 73G35HSL BK262 DUPONT SHENZHEN

369

Unit Price:US$ 1,445 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
20MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:lubrication｜High temperature resistance｜Filler: Glass fiber reinforced material｜35% filler by weight
Application Areas:Automotive components｜Electronic and Electrical Applications
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Multi axis Instrumented Impact Energy	23°C	ISO 6603-2	3.00 J
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	90 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	90 kJ/m²

flammability	Test Condition	Test Method	Test Result
FMVSS flammability		FMVSS302	B
Flammability level	1.5mm	IEC 60695-11-10,-20	HB
UL flame retardant rating	1.5mm	UL 94	HB
Burning rate	1.00mm	ISO 3795	24 mm/min

mechanical properties	Test Condition	Test Method	Test Result
bending strength		ISO 178	280 Mpa
Bending modulus		ISO 178	9900 Mpa
Tensile strain	Break	ISO 527-2	3.2 %
tensile strength	Break	ISO 527-2	190 Mpa
Tensile modulus		ISO 527-2	11000 Mpa

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	TD	ISO 11359-2	1.1E-04 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD	ISO 11359-2	2E-05 cm/cm/°C
Melting temperature		ISO 11357-3	221 °C
Vicat softening temperature		ISO 306/B50	215 °C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	208 °C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	220 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium,23°C,2.00mm,50%RH	ISO 62	1.8 %
Water absorption rate	Water absorption rate	Saturation,23°C,2.00mm	ISO 62	5.8 %
Shrinkage rate	MD	ISO 294-4	0.20 %
Shrinkage rate	Shrinkage rate	TD	ISO 294-4	1.0 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.