PA66 Amilan® CM3004G-30 RD TORAY JAPAN
207
- Unit Price:US$ 3,337 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:61.5MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Flame retardant｜Glass fiber reinforced｜ Glass fiber reinforced by 30%｜Filler: Glass fiber reinforced material｜Flame retardant grade｜30% filler by weight｜halogen-containing
- Application Areas:Office supplies｜Automotive sector｜building materials｜Electronic field｜Electrical field
- Color:--
- Grade:Halogen-free flame retardant grade
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | R计秤,23°C | 121 -- |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Linear coefficient of thermal expansion | ASTM D-696 | 无水｜2 10-5cm/cm.℃ | |
| ASTM D-696 | 1.3%水｜- | ||
| Heat Deflection Temperature | 18.6kg/cm2 | ASTM D-648 | 无水｜251 °C |
| 18.6kg/cm2 | ASTM D-648 | 1.3%水｜- °C | |
| melting temperature | 差示扫描测热计DSC法 | 265 °C | |
| UL-94 flame retardant grade | UL 94 | 无水｜V-0 | |
| UL 94 | 1.3%水｜- | ||
| Heat Deflection Temperature | 0.45MPa,未退火 | °C | 251 -- |
| melting temperature | °C | 265 -- | |
| Linear coefficient of thermal expansion | MD | cm/cm/°C | 2E-05 -- |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 0.40mm | V-0 -- |
| Basic performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water absorption rate | 23℃，24小时 | ASTM D-570 | 无水｜0.4 % |
| 23℃，24小时 | ASTM D-570 | 1.3%水｜- % |
| Other performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| filler content | 无水｜30 wt% | ||
| 1.3%水｜- wt% |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | -40°C | kJ/m² | 7.0 -- |
| 23°C | kJ/m² | 9.5 14 | |
| Impact strength of simply supported beam without notch | 23°C | kJ/m² | 65 70 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| volume resistivity | ASTM D-257 | 1.3%水｜8×1013 Ω.cm | |
| dielectric strength | 1/8" | ASTM D-149 | 无水｜38 KV/mm |
| 1/8" | ASTM D-149 | 1.3%水｜33 KV/mm | |
| Compared to the Leakage Traceability Index (CTI) | UL 746 | 无水｜200 V | |
| UL 746 | 1.3%水｜- V | ||
| Dissipation Factor | 106Hz | ASTM D-150 | 无水｜0.003-0.009 |
| 106Hz | ASTM D-150 | 1.3%水｜- | |
| arc resistance | 1/8" | ASTM D-495 | 无水｜70-80 S |
| 1/8" | ASTM D-495 | 1.3%水｜- S | |
| volume resistivity | ASTM D-257 | 无水｜8×1014 Ω.cm | |
| ohms·cm | 1E+15 1E+13 | ||
| dielectric strength | kV/mm | 38 33 | |
| dielectric constant | 23°C,1kHz | 4.00 -- | |
| 23°C,1MHz | 0.0100 -- | ||
| arc resistance | sec | 70.0 -- | |
| Compared to the Leakage Tracking Index (CTI) | CTI | V | PLC 3 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D-792 | 无水｜1.59 | |
| ASTM D-792 | 1.3%水｜- | ||
| 23°C | g/cm³ | 1.59 -- | |
| shrinkage rate | TD:3.00mm3 | % | 0.60-0.90 -- |
| MD:3.00mm4 | % | 0.20-0.50 -- | |
| Water absorption rate | 23°C,24hr | % | 0.60 -- |
| 饱和,23°C | % | 4.0 -- |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23℃，无缺口1/8 | 无水｜65 kg.cm/cm | |
| 23℃，无缺口1/8 | 1.3%水｜70 kg.cm/cm | ||
| tensile strength | 23℃，断裂 | ASTM D-638 | 无水｜1640 kg/cm2 |
| 23℃，断裂 | ASTM D-638 | 1.3%水｜1350 kg/cm2 | |
| Elongation at break | 23℃ | ASTM D-638 | 无水｜5 % |
| 23℃ | ASTM D-638 | 1.3%水｜5 % | |
| bending strength | 23℃ | ASTM D-790 | 无水｜2490 kg/cm2 |
| 23℃ | ASTM D-790 | 1.3%水｜2000 kg/cm2 | |
| flexural modulus | 23℃ | ASTM D-790 | 无水｜93200 kg/cm2 |
| 23℃ | ASTM D-790 | 1.3%水｜65000 kg/cm2 | |
| Tensile strain | 断裂,-40°C | % | 2.5 -- |
| 断裂,23°C | % | 3.0 3.0 | |
| 断裂,80°C | % | 4.5 -- | |
| flexural modulus | -40°C | MPa | 10200 -- |
| 23°C | MPa | 9300 6500 | |
| 80°C | MPa | 5500 -- | |
| bending strength | -40°C | MPa | 275 -- |
| 23°C | 250 MPa | ||
| 80°C | MPa | 150 -- | |
| Taber abraser | 1000Cycles | mg | 26.0 -- |
| tensile strength | -40°C | MPa | 190 -- |
| 23°C | 165 MPa | ||
| 80°C | MPa | 110 -- |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.