PC/ABS

PC/ABS WONDERLOY® PC-540J01 TAIWAN CHIMEI

234

Unit Price:US$ 3,174 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
68.5MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:heat-resisting
Application Areas:Automotive sector｜Electronic field｜Electrical field｜Home appliance components
Color:--
Grade:Flame retardant and high temperature resistant grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	23℃ (73℉)	ISO 179	40 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30℃ (-22℉)	ISO 179	12 kJ/m²
Impact strength of cantilever beam gap	23℃ (73℉)	ISO 180	40
	Impact strength of cantilever beam gap	23℃ (73℉)	ASTM D256	52
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-30℃ (-22℉)	ISO 180	12

mechanical properties	Test Condition	Test Method	Test Result
Bending modulus	2mm/m	ISO 178	2500 Mpa
Bending modulus	Bending modulus	1.3mm/m	ASTM D790	25000 kg/cm2
bending strength	2mm/mi	ISO 178	90 Mpa
bending strength	bending strength	1.3mm/m	ASTM D790	900 kg/cm2
Elongation at Break	50mm/m	ISO 527	1.2
Elongation at Break	Elongation at Break	50mm/m	ASTM D638	1
tensile strength	50mm/mi，Break	ISO 527	55 Mpa
	tensile strength	50mm/mi，Yield	ISO 527	60 Mpa
	tensile strength	tensile strength	50mm/mi，Yield	ASTM D638	600 kg/cm2

thermal properties	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	Flow:23-5，Flow	ISO 11359-2	80 °C
Vicat softening temperature	5KG,50℃	ISO 306	101 °C
	Vicat softening temperature	1KG,50℃	ISO 306	107 °C
		Vicat softening temperature	5KG,50℃	ASTM D1525	101 °C
		Vicat softening temperature	Vicat softening temperature	1KG,50℃/	ASTM D1525	107 °C

combustion performance	Test Condition	Test Method	Test Result
UL fire rating V		UL 94	1.5 mm
UL fire rating 5VB		UL 94	2 mm
UL flame retardant rating	5VA	UL 94	3 mm

Physical properties	Test Condition	Test Method	Test Result
Melt Volume Flow Rate (MVR)	260°C/2.16 kg	ISO 1133	20 cm³/10 min
melt mass-flow rate	260°C/2.16 kg	ASTM D1238	21 g/10min
Melt Volume Flow Rate (MVR)	260°C/2.16 kg	ISO 1133	20 cm³/10 min
Shrinkage rate		ASTM D 955	0.4-0.6 %
melt mass-flow rate	260°C/2.16 kg	ISO 1133	21

Electrical Property	Test Method	Test Result
Volume resistivity	IEC 60093	390000000000000000 Ohm-m
Surface resistivity	IEC 60093	290000000000000000 Ohm
Dielectric constant	IEC 60250	3.1 -

hardness	Test Condition	Test Method	Test Result
Hardness (Rockwell R)	23℃	ISO 2039-2	119 R
Hardness (Rockwell R)	Hardness (Rockwell R)	23℃	ASTM D785	119 R

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.