Material Properties:Flame retardant｜enhance｜High mobility｜Filler: Glass fiber reinforced material｜20% filler by weight
Application Areas:Fiber grade
Color:--
Grade:Injection grade

Technical Data Sheet Compare

thermal performance	Test Condition	Test Method	Test Result
Heat Deflection Temperature	0.45MPa,未Annealed	ISO 75-2/B	141 °C
Heat Deflection Temperature	Heat Deflection Temperature	1.8MPa,未Annealed	ISO 75-2/A	137 °C

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.75mm	UL 94	V-2
UL flame retardant rating	UL flame retardant rating	1.5mm	UL 94	V-0

Physical properties	Test Condition	Test Method	Test Result
shrinkage rate	TD:3.20mm		0.25-0.45 %
shrinkage rate	shrinkage rate	MD:3.20mm		0.15-0.35 %
water absorption rate	Saturation,23°C	ISO 62	0.11 %

Electrical performance	Test Condition	Test Method	Test Result
Compared to the Leakage Tracking Index (CTI)	CTI	UL 746	PLC 3

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	Break	ISO 527-2	90.0 Mpa
Tensile strain	Break	ISO 527-2	2.9 %
flexural modulus		ISO 178	5500 Mpa
bending strength		ISO 178	139 Mpa

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C	ISO 179	39 kJ/m²

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.