'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
TPEE RITEFLEX® 640 CELANESE USA
303
- Unit Price:US$ 4,700 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:31MT
- Delivery Terms:FOB
- Port of Loading :Guangzhou port, China
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
+86 ********View
For more details, please contact the supplier!
Material Description
- Material Properties:UV resistance
- Application Areas:Automotive components｜High temperature hot plugging adhesive
- Color:--
- Grade:Injection grade
Technical Data Sheet
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak | |
| 23°C | ISO 179/1eU | NoBreak | ||
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | NoBreak | |
| 23°C | ISO 180/1U | NoBreak | ||
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| UL flame retardant rating | 1.5mm | UL 94 | HB | |
| elastomer | Test Condition | Test Method | Test Result | Test Unit |
| tear strength | ASTM D624 | 126 | kN/m | |
| Flow | ISO 34-1 | 84 | kN/m | |
| Shore hardness | ASTM D2632 | 59 | % | |
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| Tensile modulus | ISO 527-2/1A/1 | 75.0 | Mpa | |
| tensile strength | Break,23°C | ASTM D638 | 20.7 | Mpa |
| Break | ISO 527-2/1A/50 | 17.0 | Mpa | |
| 5.0%Strain | ISO 527-2 | 3.00 | Mpa | |
| 10%Strain | ISO 527-2 | 5.00 | Mpa | |
| 50%Strain | ISO 527-2/1A/50 | 8.00 | Mpa | |
| elongation | Break,23°C | ASTM D638 | 480 | % |
| Tensile strain | Break | ISO 527-2/1A/50 | >300 | % |
| Bending modulus | -40°C | ISO 178 | 115 | Mpa |
| 23°C | ISO 178 | 70.0 | Mpa | |
| bending strength | 3.5%Strain | ISO 178 | 3.00 | Mpa |
| 23°C | ISO 178 | 5.00 | Mpa | |
| Taber wear resistance | 1000Cycles,CS-18Wheel | ASTM D4060 | 90.0 | mg |
| RossFlex | Internal Method | >1.0E+6 | cycles | |
| Tensile modulus | 23°C | ASTM D638 | 92.4 | Mpa |
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| Vicat softening temperature | ASTM D1525 | 136 | °C | |
| Melting temperature | ASTM D3418 | 180 | °C | |
| ISO 11357-3 | 170 | °C | ||
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 2.2E-04 | cm/cm/°C |
| Hot deformation temperature | 0.45MPa,Unannealed | ISO 75-2/B | 56.0 | °C |
| Brittle temperature | ISO 974 | -78.0 | °C | |
| Glass transition temperature | ASTM D3418 | -65.0 | °C | |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| Specific volume | ASTM D792 | 0.882 | cm³/g | |
| melt mass-flow rate | ASTM D1238 | 8.0to12 | g/10min | |
| 220°C/2.16kg | ISO 1133 | 10 | g/10min | |
| Shrinkage rate | MD | ASTM D955 | 1.0 | % |
| MD | ISO 294-4 | 1.2-1.4 | % | |
| shear strength | Internal Method | 1000 | 1/°C | |
| viscosity | Internal Method | 351 | Pa·s | |
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| Surface resistivity | IEC 60093 | 3E+15 | ohms | |
| Volume resistivity | ASTM D257 | 5E+12 | ohms·cm | |
| IEC 60093 | 5E+12 | ohms·cm | ||
| Dielectric strength | ASTM D149 | 12 | KV/mm | |
| IEC 60243-1 | 13 | KV/mm | ||
| Relative permittivity | 1MHz | IEC 60250 | 4.70 | |
| Dissipation factor | 1MHz | IEC 60250 | 0.030 | |
| Compared to the anti leakage trace index | ASTM D3638 | PLC 0 | ||
| IEC 60112 | PLC 0 | |||
| hardness | Test Condition | Test Method | Test Result | Test Unit |
| Shore hardness | ShoreD | ASTM D2240 | 40 | |
| ShoreD,15Sec | ISO 868 | 40 | ||
| Internal Method | 40.0 | |||
| Supplementary Information | Test Condition | Test Method | Test Result | Test Unit |
| tear strength | Kg/m | 110.3 | kN/m | |
| temperature | Internal Method | 220 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.