'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
POM Delrin® 500P NC010 DUPONT NETHERLANDS
6
- Unit Price:US$ 3,390 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:66MT
- Delivery Terms:FOB
- Port of Loading :Dongguan Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
- Material Comparison:
Transaction Guarantee:
Supplier Information
Dongguan Jinghan Polymer Materials Co., Ltd
+86 755 ********View
serv********View
+86 ********View
For more details, please contact the supplier!
Material Description
- Material Properties:High rigidity｜Aging resistance｜currency｜Weather resistance
- Application Areas:Automotive sector｜Fitness equipment
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| Multi axis Instrumented Impact Energy | 23°C | ISO 6603-2 | 3.00 | J |
| Multi axis Instrumented Peak Impact Force | 23°C | ISO 6603-2 | 2000 | N |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 280 | kJ/m² |
| -30°C | ISO 180/1U | 250 | kJ/m² | |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 8.0 | kJ/m² |
| 23°C | ISO 179/1eA | 9.0 | kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 280 | kJ/m² |
| 23°C | ISO 179/1eU | 320 | kJ/m² | |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 8.0 | kJ/m² |
| 23°C | ISO 180/1A | 9.0 | kJ/m² | |
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| Atomization | G-value(condensate) | ISO 6452 | 3.5E-04 | g |
| F-value(refraction) | ISO 6452 | 90 | % | |
| FMVSS flammability | FMVSS302 | B | ||
| Extreme Oxygen Index | ISO 4589-2 | 22 | % | |
| UL flame retardant rating | 1.5mm | IEC 60695-11-10,-20 | HB | |
| 0.8mm | IEC 60695-11-10,-20 | HB | ||
| Burning rate | 1.00mm | ISO 3795 | 20 | mm/min |
| UL flame retardant rating | 0.8mm | UL 94 | HB | |
| 1.5mm | UL 94 | HB | ||
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| Tensile creep modulus | 1hr | ISO 899-1 | 2800 | Mpa |
| Nominal tensile fracture strain | ISO 527-2 | 30 | % | |
| Tensile strain | Yield | ISO 527-2 | 17 | % |
| tensile strength | Yield | ISO 527-2 | 71.0 | Mpa |
| Tensile modulus | ISO 527-2 | 3100 | Mpa | |
| Tensile creep modulus | 1000hr | ISO 899-1 | 1600 | Mpa |
| Bending modulus | ISO 178 | 3000 | Mpa | |
| bending strength | 3.5%Strain | ISO 178 | 80.0 | Mpa |
| Poisson's ratio | ISO 527 | 0.35 | ||
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| Hot deformation temperature | 0.45MPa,Unannealed | ISO 75-2/B | 160 | °C |
| 1.8MPa,Unannealed | ISO 75-2/A | 95.0 | °C | |
| Vicat softening temperature | ISO 306/B50 | 155 | °C | |
| Ball Pressure Test | 165°C | IEC 60695-10-2 | Pass | |
| Melting temperature | ISO 11357-3 | 178 | °C | |
| Linear coefficient of thermal expansion | MD：-- | ISO 11359-2 | 1E-04 | cm/cm/°C |
| MD：-40to23°C | ISO 11359-2 | 9E-05 | cm/cm/°C | |
| TD：-- | ISO 11359-2 | 1E-04 | cm/cm/°C | |
| TD：-40to23°C | ISO 11359-2 | 9E-05 | cm/cm/°C | |
| TD：AnnealingTemperature | ISO 11359-2 | 160 | °C | |
| TD：AnnealingTime-Optional | ISO 11359-2 | 30.0 | min/mm | |
| TD：EffectiveThermalDiffusivity | ISO 11359-2 | 9E-08 | m²/s | |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| ThermalConductivityofMelt | 0.24 | W/m/K | ||
| MediumDensity | 1.19 | g/cm³ | ||
| Water absorption rate | Equilibrium,23°C,2.00mm,50%RH | ISO 62 | 0.40 | % |
| Saturation,23°C,2.00mm | ISO 62 | 1.4 | % | |
| Shrinkage rate | MD | ISO 294-4 | 2.0 | % |
| TD | ISO 294-4 | 1.9 | % | |
| Melt Volume Flow Rate (MVR) | 190°C/2.16kg | ISO 1133 | 13.0 | cm3/10min |
| melt mass-flow rate | ISO 1133 | 15 | g/10min | |
| density | ISO 1183 | 1.42 | g/cm³ | |
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| Surface resistivity | IEC 60093 | 4E+14 | ohms | |
| Volume resistivity | IEC 60093 | 2E+14 | ohms·cm | |
| Dissipation factor | 1MHz | IEC 60250 | 5.5E-03 | |
| Compared to the anti leakage trace index | IEC 60112 | PLC 0 | ||
| Dielectric strength | IEC 60243-1 | 44 | KV/mm | |
| Relative permittivity | 100Hz | IEC 60250 | 3.80 | |
| 1MHz | IEC 60250 | 3.80 | ||
| Dissipation factor | 100Hz | IEC 60250 | 9E-03 | |
| hardness | Test Condition | Test Method | Test Result | Test Unit |
| Rockwell hardness | M-Sale | ISO 2039-2 | 92 | |
| R-Sale | ISO 2039-2 | 120 | ||
| Ball Pressure Test | H358/30 | ISO 2039-1 | 192 | Mpa |
| Supplementary Information | Test Condition | Test Method | Test Result | Test Unit |
| EmissionofOrganicCompounds | VDA277 | 3.10 | µgC/g | |
| Emission | VDA275 | <8.00 | mg/kg |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.