PC LEXAN™ EXL1414T NA8A005T SABIC INNOVATIVE US
199
- Unit Price:US$ 3,060 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:45MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Low temperature resistance｜transparent｜Processability｜Moderate liquidity｜Ductility｜copolymer
- Application Areas:Electrical field｜Electronic field｜Household appliances｜Household appliances｜Bottle cap
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | L 计秤 | ISO 2039-2 | 87 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| RTI | UL 746 | 130 °C | |
| RTI Elec | UL 746 | 130 °C | |
| Linear coefficient of thermal expansion | 横向 : 23 到 80°C | ISO 11359-2 | 8.0E-5 cm/cm/°C |
| 横向 : -40 到 95°C | ASTM E831 | 8.0E-5 cm/cm/°C | |
| 流动 : 23 到 80°C | ISO 11359-2 | 6.7E-5 cm/cm/°C | |
| 流动 : -40 到 95°C | ASTM E831 | 6.7E-5 cm/cm/°C | |
| ball-indentation hardness | 123 到 127°C | IEC 60695-10-2 | 通过 |
| vicat | -- | ISO 306/B120 | 139 °C |
| Heat Deflection Temperature | 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距9 | ISO 75-2/Af | 116 °C |
| vicat | -- | ASTM D152510 | 138 °C |
| Heat Deflection Temperature | 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 120 °C |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Haze ratio | 2540 µm | ASTM D1003 | 3.0 % |
| transmissivity | 2540 µm | ASTM D1003 | 82.0 % |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Burning wire flammability index | 3.0 mm | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | 0.8 mm | IEC 60695-2-13 | 850 °C |
| UL flame retardant rating | 0.8 mm | UL 94 | HB |
| Hot filament ignition temperature | 3.0 mm | IEC 60695-2-13 | 850 °C |
| UL flame retardant rating | 3.0 mm | UL 94 | V-2 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 无断裂 |
| Dart impact | -30°C, Total Energy | ASTM D3763 | 77.0 J |
| 23°C, Total Energy | ASTM D3763 | 75.0 J | |
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 无断裂 |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 无断裂 |
| 23°C | ISO 179/1eU | 无断裂 | |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 70 kJ/m² |
| -30°C | ISO 179/1eA | 60 kJ/m² |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Exhaust hole depth | 0.025 to 0.076 mm | ||
| Back pressure | 0.300 to 0.700 Mpa | ||
| screw speed | 40 to 70 rpm | ||
| mold temperature | 70 to 95 °C | ||
| Spray nozzle temperature | 290 to 310 °C | ||
| Processing (melt) temperature | 295 to 315 °C | ||
| Temperature at the front of the material cylinder | 295 to 315 °C | ||
| Temperature in the middle of the barrel | 280 to 305 °C | ||
| Temperature at the rear of the barrel | 270 to 295 °C | ||
| Suggested maximum moisture content | 0.020 % | ||
| Suggested injection volume | 40 to 60 % | ||
| drying time | 3.0 to 4.0 hr | ||
| drying temperature | 120 °C |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | 300°C/1.2 kg | ASTM D1238 | 10 g/10 min |
| Melt volume flow rate | 300°C/1.2 kg | ISO 1133 | 9.00 cm3/10min |
| shrinkage rate | 流动 : 3.20 mm | 内部方法 | 0.40 - 0.80 % |
| 横向流动 : 3.20 mm | 内部方法 | 0.40 - 0.80 % | |
| Water absorption rate | 饱和, 23°C | ISO 62 | 0.12 % |
| 平衡, 23°C, 50% RH | ISO 62 | 0.090 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| volume resistivity | ASTM D257 | > 1.0E+15 ohms·cm | |
| Surface Resistivity | ASTM D257 | > 1.0E+15 ohms |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| bending strength | 屈服, 50.0 mm 跨距4 | ASTM D790 | 92.0 Mpa |
| flexural modulus | --5 | ISO 178 | 2120 Mpa |
| bending strength | --5,6 | ISO 178 | 88.0 Mpa |
| flexural modulus | 50.0 mm 跨距4 | ASTM D790 | 2180 Mpa |
| elongation | 断裂 | ISO 527-2/50 | 110 % |
| 断裂3 | ASTM D638 | 120 % | |
| 屈服 | ISO 527-2/50 | 5.4 % | |
| 屈服3 | ASTM D638 | 5.6 % | |
| tensile strength | 断裂 | ISO 527-2/50 | 55.0 Mpa |
| 断裂3 | ASTM D638 | 59.0 Mpa | |
| 屈服 | ISO 527-2/50 | 56.0 Mpa | |
| Tensile modulus | -- | ISO 527-2/1 | 2300 Mpa |
| tensile strength | 屈服3 | ASTM D638 | 57.0 Mpa |
| Tensile modulus | --2 | ASTM D638 | 2180 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.