PBT CELANEX® 2008 CELANESE USA
6
- Unit Price:US$ 3,646 /MT
- Packaging Specification:
- Supply Quantity:33MT
- Delivery Terms:DDP
- :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High mobility｜Easy to process
- Application Areas:Electronic and electrical accessories｜Automotive sector｜currency
- Color:--
- Grade:--
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | M级 | ISO 2039-2 | 72 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO 75-2/B | 155 °C |
| 0.45MPa,退火 | ASTM D648 | 154 °C | |
| 1.8MPa,未退火 | ASTM D648 | 54.4 °C | |
| 1.8MPa,未退火 | ISO 75-2/A | 57.0 °C | |
| Glass Transition Temperature | ISO 11357-2 | 60.0 °C | |
| melting temperature | ASTM D3418 | 225 °C | |
| ISO 11357-3 | 225 °C | ||
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.1E-04 cm/cm/°C |
| TD | ISO 11359-2 | 1E-04 cm/cm/°C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 2.1 kJ/m² |
| 23°C | ISO 179/1eA | 2.8 kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 44 kJ/m² |
| 23°C | ISO 179/1eU | 38 kJ/m² | |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 3.1 kJ/m² |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| shrinkage rate | MD | ASTM D955 | 1.8-2.0 % |
| TD | ISO 294-4 | 1.8-2.0 % | |
| MD | ISO 294-4 | 1.8-2.0 % | |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.17 % |
| density | ASTM D792 | 1.31 g/cm³ | |
| ISO 1183 | 1.31 g/cm³ |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| dielectric strength | ASTM D149 | 16 KV/mm | |
| IEC 60243-1 | 15 KV/mm | ||
| dielectric constant | 1MHz | ASTM D150 | 3.20 |
| relative permittivity | 100Hz | IEC 60250 | 3.30 |
| 1MHz | IEC 60250 | 3.20 | |
| Dissipation Factor | 1MHz | ASTM D150 | 1E-03 |
| 1MHz | IEC 60250 | 0.020 | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 2 | |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| volume resistivity | ASTM D257 | 1E+16 ohms·cm |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1A/1 | 2600 Mpa | |
| tensile strength | 屈服,23°C | ASTM D638 | 55.2 Mpa |
| 断裂 | ISO 527-2/1A/5 | 60.0 Mpa | |
| 断裂 | ISO 527-2/1A/50 | 47.0 Mpa | |
| elongation | 断裂,23°C | ASTM D638 | 5.0 % |
| Tensile strain | 断裂 | ISO 527-2/1A/5 | 5.0 % |
| 断裂 | ISO 527-2/1A/50 | 2.0 % | |
| flexural modulus | 23°C | ISO 178 | 2200 Mpa |
| bending strength | 23°C | ISO 178 | 80.0 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.