Material Properties:Glass fiber reinforced｜dimensional stability ｜High rigidity｜high strength｜heat-resisting
Application Areas:Lawn equipment｜Garden equipment｜Industrial applications｜Automotive External Parts｜Electrical field｜Electronic field｜Architectural application field｜Outdoor applications｜Electrical appliances｜Engine hood parts｜Medical supplies｜Nursing supplies｜Plastic bag｜Automotive interior parts｜Casters｜Household goods｜Petroleum Applications｜Natural gas supplies｜sporting goods｜Textile application｜Lighting applications
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	45	kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	45	kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179/1eA	5.0	kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/1A	8.0	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	45	kJ/m²
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	7.0	kJ/m²
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	5.0	kJ/m²
Impact strength of cantilever beam gap	-30°C	ASTM D256	80	J/m
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength	Yield	ASTM D638	120	Mpa
Tensile modulus		ISO 527-2/1	9300	Mpa
Tensile strain	Yield	ASTM D638	2.7	%
bending strength	Yield,50.0mmSpan	ASTM D790	195	Mpa
	bending strength	Break,50.0mmSpan	ASTM D790	190	Mpa
	bending strength	bending strength		ISO 178	195	Mpa
Bending modulus		ISO 178	8500	Mpa
Tensile strain	Yield	ISO 527-2/5	2.0	%
Taber abraser	1000Cycles,1000g,CS-17Wheel	ASTM D1044	19.0	mg
tensile strength	Break	ASTM D638	120	Mpa
Tensile modulus		ASTM D638	9300	Mpa
Tensile strain	Break	ASTM D638	2.7	%
tensile strength	Break	ISO 527-2/5	125	Mpa
Bending modulus	50.0mmSpan	ASTM D790	7580	Mpa
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	MD：--4	Internal Method	0.50-0.80	%
density		ASTM D792	1.53	g/cm³
Shrinkage rate	MD：--2	Internal Method	0.30-0.70	%
Shrinkage rate	Shrinkage rate	MD：3.20mm	Internal Method	0.30-0.80	%
Specific volume		ASTM D792	0.660	cm³/g
Shrinkage rate	TD：--3	Internal Method	0.40-0.60	%
Shrinkage rate	Shrinkage rate	MD：--3	Internal Method	0.30-0.50	%
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.080	%
Shrinkage rate	TD：--2	Internal Method	0.50-1.0	%
Water absorption rate	24hr	ASTM D570	0.090	%
Shrinkage rate	TD：--5	Internal Method	0.60-0.90	%
melt mass-flow rate	250°C/2.16kg	ISO 1133	17	g/10min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.