PC LUPOY® GP2102 LG GUANGZHOU
307
- Unit Price:US$ 3,578 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:60MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Glass fiber reinforced｜Chemical resistance
- Application Areas:Electrical field｜Electronic field
- Color:--
- Grade:--
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | ASTM D785 | 124 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | ASTM D648 | 137 °C | |
| RTI Elec | UL 746 | 80.0 °C | |
| RTI Imp | UL 746 | 80.0 °C | |
| RTI | UL 746 | 80.0 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | ASTM D638 | 53.9 Mpa | |
| elongation | ASTM D638 | 15 % | |
| flexural modulus | ASTM D790 | 3330 Mpa | |
| bending strength | ASTM D790 | 98.1 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256 | 270 J/m |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792 | 1.25 g/cm³ | |
| melt mass-flow rate | ASTM D1238 | 9.0 g/10 min | |
| shrinkage rate | ASTM D955 | 0.20 - 0.40 % |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 100 to 120 °C | ||
| drying time | 3.0 to 5.0 hr | ||
| Suggested maximum moisture content | 0.020 % | ||
| Minimum Moisture Content | 0.020 % | ||
| Temperature at the rear of the barrel | 280 to 295 °C | ||
| Temperature in the middle of the barrel | 285 to 300 °C | ||
| Temperature at the front of the material cylinder | 290 to 305 °C | ||
| Spray nozzle temperature | 290 to 305 °C | ||
| Processing (melt) temperature | 295 to 310 °C | ||
| mold temperature | 90 to 110 °C | ||
| Back pressure | 0.981 to 3.92 Mpa | ||
| screw speed | 40 to 70 rpm |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.