Material Description

Material Properties:Thermal stability｜Dimensional stability
Application Areas:Electrical applications｜Fitness equipment
Color:--
Grade:Injection grade

Technical Data Sheet

Filling analysis	Test Method	Test Result
Melt density		1.40 g/cm³
Top out temperature		210 °C
Specific Heat Capacity of Melt		1870 J/kg/°C
Thermal Conductivity of Melt		0.31 W/m/K
Emission of Organic Compounds	VDA 277	6.50 µgC/g
Odor	VDA 270	3.00

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	100 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	90 kJ/m²

flammability	Test Condition	Test Method	Test Result
FMVSS combustion rate		FMVSS 302	SE
雾化 - G-value (condensate)		ISO 6452	4.0E-4 g
Extreme Oxygen Index		ISO 4589-2	24 %
UL flame retardant rating		UL 94	HB
UL flame retardant rating	UL flame retardant rating		UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
Tensile creep modulus	1000 hr	ISO 899-1	-- Mpa
Tensile creep modulus	Tensile creep modulus	1 hr	ISO 899-1	-- Mpa
Tensile strain	Break	ISO 527-2	2.3 %
tensile strength	Break	ISO 527-2	250 Mpa
Tensile modulus		ISO 527-2	17000 Mpa

injection	Test Condition	Test Method	Test Result
drying temperature			80 °C
Drying time - hot air dryer			2.0 to 4.0 hr
Suggested maximum moisture content			0.20 %
Processing (melt) temperature			285 to 305 °C
Melt Temperature, Optimum			295 °C
Mold temperature			50 to 90 °C
Mold Temperature, Optimum			100 °C
Maintain pressure			50.0 to 100 Mpa
Maintain pressure	Maintain pressure	Drying Recommended		yes
Hold Pressure Time			3.00 s/mm
Maximum Screw Tangential Speed			12 m/min

thermal performance	Test Condition	Test Method	Test Result
thermal conductivity			0.46 W/m/K
Linear coefficient of thermal expansion	Across Flow	ISO 11359-2	7.5E-5 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Flow	ISO 11359-2	1.5E-5 cm/cm/°C
Melting temperature		ISO 11357-3	262 °C
Vicat softening temperature		ISO 306/B50	255 °C
Glass transition temperature		ISO 11357-2	80.0 °C
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	260 °C
Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	262 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium, 23°C, 2.00 mm, 50% RH	ISO 62	1.2 %
Water absorption rate	Water absorption rate	Saturation, 23°C, 2.00 mm	ISO 62	4.2 %
Shrinkage rate	Flow	ISO 294-4	0.30 %
Shrinkage rate	Shrinkage rate	横向Flow	ISO 294-4	0.80 %

Electrical performance	Test Condition	Test Method	Test Result
Volume resistivity		IEC 62631-3-1	1.0E+13 ohms·m
Surface resistivity		IEC 62631-3-2	-- ohms

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.