ABS

ABS POLYLAC® PA-727 TAIWAN CHIMEI

773

Unit Price:US$ 2,071 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
358.3MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

For more details, please contact the supplier!

Material Description

Material Properties:High gloss｜High toughness｜High rigidity
Application Areas:Automotive sector｜Sanitary Ware｜Household goods
Color:--
Grade:Electroplating grade

Material Certification

SGS

RoHS

Technical Data Sheet

other	Test Condition	Test Method	Test Result
remarks			在射出周期中勿将热融胶长期停留在加热管中
characteristic			电镀性能佳。
Color			-
purpose			通用于一切需要电镀装饰配件按纽、音响器材面板、轮胎盖、镜框、时钟外壳和汽车配件等

machinability	Test Condition	Test Method	Test Result
Dry conditions			于85°C下烘料约3-4小时
Processing temperature			180-220 °C
	Processing temperature			190-230 °C
	Processing temperature	Processing temperature			180-230°C °C
Screw speed			- rpm
Mold temperature			30-70°C °C
Melt Temperature			- °C
pressure			- Mpa

mechanical properties	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap		ASTM D256/ISO 179	- kg·cm/cm(J/M)ft·lb/in
Elongation at Break		ASTM D638/ISO 527	- %
Tensile modulus		ASTM D638/ISO 527	- kg/cm²(MPa)[Lb/in²]
tensile strength		ASTM D638/ISO 527	485(6870) kg/cm²(MPa)[Lb/in²]
elongation		ASTM D638/ISO 527	20 %
Rockwell hardness		ASTM D785	R-110
Bending modulus		ASTM D790/ISO 178	2700(38000) kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	780(11.000) kg/cm²(MPa)[Lb/in²]
Charpy Notched Impact Strength		ASTM D256/ISO 179	- kg·cm/cm(J/M)ft·lb/in
Impact strength of cantilever beam gap		ASTM D256/ISO 179	23(4.2) kg·cm/cm(J/M)ft·lb/in
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ASTM D256/ISO 179	26(4、8) kg·cm/cm(J/M)ft·lb/in
Elongation at Break		ASTM D638/ISO 527	- %

thermal performance	Test Condition	Test Method	Test Result
Combustibility (rate)		UL 94	1/16“HB
Hot deformation temperature	HDT	ASTM D648/ISO 75	99(210) ℃（℉）
Hot deformation temperature	Hot deformation temperature	HDT	ASTM D648/ISO 75	88(190) ℃（℉）
Vicat softening temperature		ASTM D1525/ISO R306	105(221) ℃（℉）
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	- mm/mm.℃

Physical properties	Test Condition	Test Method	Test Result
density		ASTM D792/ISO 1183	1.04
Shrinkage rate		ASTM D955	- %
Water absorption rate		ASTM D570/ISO 62	- %
melt mass-flow rate		ASTM D1238/ISO 1133	1.8 g/10min
melt mass-flow rate	melt mass-flow rate		ASTM D1238/ISO 1133	19 g/10min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.