PBT Ultradur® B 4040 G4 BK BASF GERMANY
193
- Unit Price:US$ 3,751 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:32MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Flame retardant enhanced grade
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ball-indentation hardness | H358/30 | ISO 2039-1 | 190 Mpa |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| maximum service temperature | 短周期操作 | 210 °C | |
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO 75-2/B | 215 °C |
| 1.8MPa,未退火 | ISO 75-2/A | 180 °C | |
| melting temperature | ISO 11357-3 | 223 °C | |
| Linear coefficient of thermal expansion | MD：23到80°C | ISO 11359-2 | 2.0E-5到3.0E-5 cm/cm/°C |
| specific heat | 1100 J/kg/°C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Flammability level | 0.75mm | IEC 60695-11-10,-20 | HB |
| 1.6mm | IEC 60695-11-10,-20 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 5.5 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 40 kJ/m² |
| 23°C | ISO 179/1eU | 40 kJ/m² |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| shrinkage rate | MD | ISO 294-4 | 0.40 % |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.40 % |
| 平衡,23°C,50%RH | ISO 62 | 0.20 % | |
| viscosity number | ISO 307 | 105 cm³/g | |
| shrinkage rate | free,longitudinal | 0.21 % | |
| free,transverse | 1.1 % | ||
| density | ISO 1183 | 1.47 g/cm³ | |
| Apparent density | 0.70to0.80 g/cm³ | ||
| Melt volume flow rate | 275°C/2.16kg | ISO 1133 | 22.0 cm3/10min |
| shrinkage rate | TD | ISO 294-4 | 0.90 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | 1E+13 ohms | |
| volume resistivity | IEC 60093 | 1E+16 ohms·cm | |
| relative permittivity | 100Hz | IEC 60250 | 3.70 |
| 1MHz | IEC 60250 | 3.50 | |
| Dissipation Factor | 100Hz | IEC 60250 | 1.4E-03 |
| 1MHz | IEC 60250 | 0.018 | |
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 2 |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 7500 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 120 Mpa |
| Tensile strain | 断裂 | ISO 527-2 | 2.8 % |
| flexural modulus | ISO 178 | 7010 Mpa | |
| bending strength | ISO 178 | 190 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.