Material Description

Material Properties:High mobility｜Low crud
Application Areas:Automotive components｜Electronic and electrical accessories
Color:--
Grade:Impact resistant grade

Technical Data Sheet

Filling analysis	Test Condition	Test Method	Test Result
Top out temperature			210 °C
Thermal Conductivity of Melt			0.25 W/m/K

impact performance	Test Condition	Test Method	Test Result
Multi axis Instrumented Impact Energy	23°C	ISO 6603-2	4.40 J
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	90 kJ/m²

flammability	Test Condition	Test Method	Test Result
FMVSS combustion rate		FMVSS 302	B
Extreme Oxygen Index		ISO 4589-2	24 %
Burning rate	1.00 mm	ISO 3795	27 mm/min

mechanical properties	Test Condition	Test Method	Test Result
bending strength		ISO 178	340 Mpa
Bending modulus		ISO 178	12500 Mpa
Tensile strain	Break	ISO 527-2	2.5 %
tensile strength	Break	ISO 527-2	225 Mpa
Tensile modulus		ISO 527-2	14000 Mpa

injection	Test Condition	Test Method	Test Result
drying temperature			80 °C
Drying time - hot air dryer			2.0 to 4.0 hr
Suggested maximum moisture content			0.20 %
Processing (melt) temperature			285 to 300 °C
Melt Temperature, Optimum			295 °C
Mold temperature			70 to 120 °C
Mold Temperature, Optimum			100 °C
Maintain pressure			50.0 to 100 Mpa
Maintain pressure	Maintain pressure	Drying Recommended		yes
Hold Pressure Time			3.00 s/mm
Maximum Screw Tangential Speed			12 m/min

thermal performance	Test Condition	Test Method	Test Result
Melting temperature		ISO 11357-3	262 °C
Glass transition temperature		ISO 11357-2	80.0 °C
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	255 °C
Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	258 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium, 23°C, 2.00 mm, 50% RH	ISO 62	1.5 %
	Water absorption rate	Saturation, 23°C, 2.00 mm	ISO 62	4.7 %
	Water absorption rate	Water absorption rate	24 hr, 23°C, 2.00 mm	ISO 62	0.90 %
Shrinkage rate	Flow	ISO 294-4	0.30 %
Shrinkage rate	Shrinkage rate	横向Flow	ISO 294-4	0.90 %

Electrical performance	Test Condition	Test Method	Test Result
Compared to the anti leakage trace index		IEC 60112	V
Dissipation factor	1 MHz	IEC 62631-2-1	0.015
Dissipation factor	Dissipation factor	100 Hz	IEC 62631-2-1	0.013
Dielectric strength		IEC 60243-1	25 KV/mm
Volume resistivity		IEC 62631-3-1	> 1.0E+13 ohms·m

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.