POM Iupital™ FW-24 MITSUBISHI ENGINEERING JAPAN
200
- Unit Price:US$ 2,571 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:40MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:wear resistant｜High mobility
- Application Areas:Automotive sector｜Electronic and Electrical Applications
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | 2.0 % | ||
| Water absorption rate | ASTM D570 | 0.22 % | |
| melt mass-flow rate | ASTM D1238 | 9.5 g/10min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | ASTM D638 | 51 Mpa | |
| Stretching length | ASTM D638 | 50 % | |
| bending strength | ASTM D790 | 73.5 Mpa | |
| Flexural modulus | ASTM D790 | 2.45 GPa | |
| Impact strength of cantilever beam gap | ASTM D256 | 49 J/m | |
| Rockwell hardness | ASTM D785 | 80 M |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| dielectric constant | ASTM D150 | - Pf/m | |
| Surface Resistivity | ASTM D257 | 1×10 | |
| Volume resistivity | ASTM D257 | 1×10 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ASTM D648 | 156 °C | |
| ASTM D648 | 107 °C | ||
| UL flame retardant rating | UL 94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.