PBT TRIBIT® 1500G15 SAMYANG KOREA
187
- Unit Price:US$ 2,346 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Medium viscosity
- Application Areas:Laptop case｜Automotive sector｜Phone case｜Engine parts
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water absorption rate | ASTM D-570 | 0.08 % | |
| melt mass-flow rate | ASTM D1238 | 85 g/10min | |
| Shrinkage rate | ASTM D955 | 0.20-1.2 % | |
| Water absorption rate | ASTM D570 | 0.080 % |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | ASTM D785 | 119 |
| other | Test Condition | Test Method | Test Result |
|---|---|---|---|
| characteristic | 玻纤增强 |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Flexural modulus | ASTM D-790 | 50000 kg/cm | |
| Rockwell hardness | ASTM D-785 | 119 R scale | |
| bending strength | ASTM D-790 | 1500 kg/cm | |
| elongation | ASTM D-638 | 7 % | |
| Impact strength of cantilever beam gap | ASTM D-256 | 1/8＂英寸 kg.cm/cm | |
| tensile strength | ASTM D-638 | 1100 kg/cm | |
| ASTM D638 | 108 Mpa | ||
| elongation | ASTM D638 | 7.0 % | |
| Flexural modulus | ASTM D790 | 4900 Mpa | |
| bending strength | ASTM D790 | 147 Mpa | |
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 7 kg·cm/cm(J/M)ft·lb/in | |
| elongation at break | ASTM D638/ISO 527 | 7 % | |
| tensile strength | ASTM D638/ISO 527 | 1100 kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | ASTM D785 | 119 | |
| Flexural modulus | ASTM D790/ISO 178 | 50000 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 1500 kg/cm²(MPa)[Lb/in²] |
| Other performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL -94 | HB | |
| Conductivity | ASTM D-150 | 3.2 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| arc resistance | ASTM D-495 | 150 sec | |
| Dissipation Factor | ASTM D-150 | 0.02 | |
| Volume resistivity | ASTM D-257 | 10 Ω.cm | |
| dielectric strength | ASTM D-257 | 21 KV/mm | |
| Volume resistivity | ASTM D257 | 1E+16 ohms·cm | |
| dielectric strength | ASTM D149 | 21 KV/mm | |
| dielectric constant | ASTM D150 | 3.20 | |
| Dissipation Factor | ASTM D150 | 0.020 | |
| arc resistance | ASTM D495 | 150 sec | |
| Volume resistivity | ASTM D257/IEC 60093 | 1 Ω.cm |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.5 | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 60 g/10min | |
| Water absorption rate | ASTM D570/ISO 62 | 0.08 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melting temperature | 224 °C | ||
| Heat distortion temperature | ASTM D-648 | 225 °C | |
| Linear coefficient of thermal expansion | ASTM D-696 | 3 mm/mm/℃ | |
| Heat distortion temperature | ASTM D-648 | 210 °C | |
| Linear coefficient of thermal expansion | ASTM D696 | 3E-05 cm/cm/°C | |
| Heat distortion temperature | ASTM D648 | 225 °C | |
| ASTM D648 | 210 °C | ||
| ASTM D648/ISO 75 | 225 ℃（℉） | ||
| ASTM D648/ISO 75 | 210 ℃（℉） | ||
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 3 mm/mm.℃ |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.