PA66 Vydyne® R535H ASCEND USA
241
- Unit Price:US$ 3,746 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:19MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | ISO 294-4 | 0.90 % | |
| ISO 294-4 | 0.40 % | ||
| Water absorption rate | ISO 62 | 0.80 % | |
| ISO 62 | 1.6 % |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| burning rate | ISO 3795 | 0.0 mm/min | |
| UL flame retardant rating | UL 94 | HB | |
| UL 94 | HB | ||
| UL 94 | HB | ||
| Burning wire flammability index | IEC 60695-2-12 | 700 °C | |
| IEC 60695-2-12 | 700 °C | ||
| IEC 60695-2-12 | 875 °C | ||
| Hot filament ignition temperature | IEC 60695-2-13 | 725 °C | |
| IEC 60695-2-13 | 725 °C | ||
| IEC 60695-2-13 | 750 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 11600 Mpa | |
| tensile strength | ISO 527-2 | 210 Mpa | |
| Tensile strain | ISO 527-2 | 3.0 % | |
| Flexural modulus | ISO 178 | 10500 Mpa | |
| bending strength | ISO 178 | 300 Mpa | |
| Poisson's ratio | ISO 527 | 0.40 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179/1eU | 70 kJ/m² | |
| ISO 179/1eU | 80 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 1.0E+13 ohms·cm | |
| dielectric strength | IEC 60243 | 20 KV/mm | |
| arc resistance | ASTM D495 | PLC 6 | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V | |
| High arc combustion index (HAI) | UL 746 | PLC 0 | |
| UL 746 | PLC 0 | ||
| UL 746 | PLC 0 | ||
| High Voltage Arc Traceability Rate (HVTR) | UL 746 | PLC 1 | |
| Hot wire ignition (HWI) | UL 746 | PLC 4 | |
| UL 746 | PLC 3 | ||
| UL 746 | PLC 4 |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 80 °C | ||
| drying time | 4.0 hr | ||
| Suggested maximum material return ratio | 25 % | ||
| Temperature at the rear of the barrel | 280 to 310 °C | ||
| Temperature in the middle of the barrel | 280 to 310 °C | ||
| Temperature at the front of the material cylinder | 280 to 310 °C | ||
| Spray nozzle temperature | 280 to 310 °C | ||
| Processing (melt) temperature | 285 to 305 °C | ||
| Temperature | 65 to 95 °C |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO 75-2/B | 260 °C | |
| ISO 75-2/A | 250 °C | ||
| melting temperature | ISO 11357-3 | 260 °C | |
| Linear coefficient of thermal expansion | ISO 11359-2 | 2.0E-5 cm/cm/°C | |
| ISO 11359-2 | 1.1E-4 cm/cm/°C | ||
| RTI Elec | UL 746 | 140 °C | |
| UL 746 | 140 °C | ||
| UL 746 | 140 °C | ||
| RTI Imp | UL 746 | 125 °C | |
| UL 746 | 125 °C | ||
| UL 746 | 125 °C | ||
| RTI | UL 746 | 140 °C | |
| UL 746 | 140 °C | ||
| UL 746 | 140 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.