PPO/PA NORYL GTX™ GTX989 SABIC INNOVATIVE US

602

Unit Price:US$ 4,940 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
90MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Hydrolysis resistance｜High temperature resistance｜Dimensional stability｜High mobility
Application Areas:Industrial machinery｜Electrical applications｜Application in the automotive field｜Automotive External Parts
Color:--
Grade:Heat resistant grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Dart impact	23°C,TotalEnergy	ASTM D3763	60.0	J
Charpy Notched Impact Strength	23°C	ISO 179/1eA	22	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179/1eA	15	kJ/m²
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus	--2	ASTM D638	2350	Mpa
bending strength	Yield,50.0mmSpan4	ASTM D790	95.0	Mpa
bending strength	bending strength	--5,6	ISO 178	90.0	Mpa
Bending modulus	--5	ISO 178	2300	Mpa
Bending modulus	Bending modulus	50.0mmSpan4	ASTM D790	2450	Mpa
elongation	Break	ISO 527-2/50	40	%
	elongation	Break3	ASTM D638	45	%
		elongation	Yield	ISO 527-2/50	5.0	%
		elongation	elongation	Yield3	ASTM D638	5.0	%
tensile strength	Break	ISO 527-2/50	55.0	Mpa
	tensile strength	Break3	ASTM D638	60.0	Mpa
		tensile strength	Yield	ISO 527-2/50	60.0	Mpa
		tensile strength	tensile strength	Yield3	ASTM D638	65.0	Mpa
Tensile modulus	--	ISO 527-2/1	2300	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Vicat softening temperature	--	ASTMD152510	195	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	200	°C
Hot deformation temperature	0.45MPa,Unannealed,100mmSpan9	ISO 75-2/Be	190	°C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	190	°C
Linear coefficient of thermal expansion	MD:-40to60°C	ASTME831	8.5E-05	cm/cm/°C
	Linear coefficient of thermal expansion	MD:23to60°C	ISO 11359-2	9E-05	cm/cm/°C
		Linear coefficient of thermal expansion	TD:-40to60°C	ASTME831	8.5E-05	cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD:23to60°C	ISO 11359-2	9E-05	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	1.2	%
Water absorption rate	Water absorption rate	Saturation,23°C	ISO 62	4.2	%
Shrinkage rate	MD：3.20mm	Internal Method	1.2-1.6	%
Melt Volume Flow Rate (MVR)	280°C/5.0kg	ISO 1133	19.0	cm3/10min
melt mass-flow rate	280°C/5.0kg	ASTM D1238	16	g/10min
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity		Internal Method	1.0E+3-1.0E+4	ohms·cm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Other Prices

Supplier	Unit Price
Dongguan Baishun	US$ 4940 /MT
Dongguan Lerui Plastic	US$ 4940 /MT
Dongguan Guangyan	US$ 5050 /MT
Dongguan Junlong	US$ 5190 /MT
Guangzhou HuShang Chemical	US$ 5610 /MT

Supplier Join

Get App

Top

PPO/PA NORYL GTX™ GTX989 SABIC INNOVATIVE US

Material Description

Technical Data Sheet

Other Prices

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index