PC LEXAN™  EXL9134 SABIC INNOVATIVE US

245
  • Unit Price:US$ 4,871 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    115.5MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:High mobility｜Ductility at low temperature｜Short molding cycle
  • Application Areas:Aerospace Applications｜Railway Applications｜Plastic bag｜Home Furnishings
  • Color:--
  • Grade:Injection grade

Material Certification

UL

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Suspended wall beam without notch impact strength-30°CISO 180/1U无断裂
Impact strength of simply supported beam without notch23°CISO 179/1eU无断裂
Impact strength of simply supported beam without notch-30°CISO 179/1eU无断裂
Charpy Notched Impact Strength23°CISO 179/1eA70 kJ/m²
Charpy Notched Impact Strength-30°CISO 179/1eA35 kJ/m²
Suspended wall beam without notch impact strength23°CISO 180/1U无断裂
Dart impact23°C, Total EnergyASTM D376367.0 J
flammabilityTest ConditionTest MethodTest Result
Hot filament ignition temperature1.5 mmIEC 60695-2-13825 °C
Hot filament ignition temperature3.0 mmIEC 60695-2-13825 °C
UL flame retardant rating1.5 mmUL 94V-0
UL flame retardant rating3.0 mmUL 945VA
Burning wire flammability index1.5 mmIEC 60695-2-12960 °C
mechanical propertiesTest ConditionTest MethodTest Result
bending strengthYield, 50.0 mm Span4ASTM D79092.0 Mpa
bending strength--5,6ISO 17887.0 Mpa
tensile strengthBreakISO 527-2/5057.0 Mpa
tensile strengthBreak3ASTM D63859.0 Mpa
tensile strengthYieldISO 527-2/5056.0 Mpa
elongationYieldISO 527-2/506.0 %
elongationYield3ASTM D6386.0 %
tensile strengthYield3ASTM D63858.0 Mpa
Tensile modulus--ISO 527-2/12000 Mpa
Tensile modulus--2ASTM D6382100 Mpa
Bending modulus--5ISO 1782100 Mpa
Bending modulus50.0 mm Span4ASTM D7902400 Mpa
elongationBreakISO 527-2/50110 %
elongationBreak3ASTM D638120 %
injectionTest ConditionTest MethodTest Result
Spray nozzle temperature290 to 310 °C
Processing (melt) temperature295 to 315 °C
Mold temperature70 to 95 °C
Back pressure0.300 to 0.700 Mpa
Screw speed40 to 70 rpm
Exhaust hole depth0.025 to 0.076 mm
Suggested injection volume40 to 60 %
Temperature at the rear of the barrel270 to 295 °C
Temperature in the middle of the barrel280 to 305 °C
Temperature at the front of the material cylinder295 to 315 °C
drying temperature120 °C
drying time3.0 to 4.0 hr
Suggested maximum moisture content0.020 %
thermal performanceTest ConditionTest MethodTest Result
Hot deformation temperature1.8 MPa, Unannealed, 3.20 mmASTM D648123 °C
Hot deformation temperature1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span9ISO 75-2/Af118 °C
Vicat softening temperature--ASTM D152510140 °C
Vicat softening temperature--ISO 306/B50139 °C
Vicat softening temperature--ISO 306/B120141 °C
Linear coefficient of thermal expansionFlow : -40 to 40°CASTM E8316.1E-5 cm/cm/°C
Linear coefficient of thermal expansionAcross Flow : -40 to 40°CASTM E8316.2E-5 cm/cm/°C
Linear coefficient of thermal expansionAcross Flow : -40°CISO 11359-26.2E-5 cm/cm/°C
RTI ElecUL 746125 °C
RTI ImpUL 746115 °C
RTIUL 746120 °C
Physical propertiesTest ConditionTest MethodTest Result
Outdoor applicabilityUL 746Cf1
Water absorption rateEquilibrium, 23°C, 50% RHISO 620.15 %
Water absorption rateSaturation, 23°CISO 620.40 %
Shrinkage rate3.20 mm，FlowInternal Method0.40 - 0.80 %
Melt Volume Flow Rate (MVR)300°C/1.2 kgISO 113315.0 cm3/10min
melt mass-flow rate300°C/1.2 kgASTM D123816 g/10 min
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.