Material Properties:Low warpage
Application Areas:Laptop case｜Electronic and Electrical Applications｜SMT application｜Communication equipment｜Card slot
Color:--
Grade:--

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	60	kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	55	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating		UL 94	V-0
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength	Break	ISO 527-2/1A/5	130	Mpa
Tensile strain	Break	ISO 527-2/1A/5	2.5	%
Bending modulus	23°C	ISO 178	13500	Mpa
Tensile modulus		ISO 527-2/1A/1	13800	Mpa
Fracture bending strain		ISO 178	2.5	%
CompressiveStress	1%Strain	ISO 604	82.0	Mpa
Compressive modulus		ISO 604	11000	Mpa
bending strength	23°C	ISO 178	180	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	TD	ISO 11359-2	1.8E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD	ISO 11359-2	6E-06	cm/cm/°C
Melting temperature		ISO 11357-3	335	°C
Vicat softening temperature		ISO 306/B50	200	°C
Hot deformation temperature	8.0MPa,Unannealed	ISO 75-2/C	220	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	265	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	2E-03	%
Water absorption rate	Water absorption rate	Saturation,23°C	ISO 62	0.015	%
Shrinkage rate	MD	ISO 294-4	0.10	%
Shrinkage rate	Shrinkage rate	TD	ISO 294-4	0.50	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dissipation factor	1MHz	IEC 60250	0.031
Relative permittivity	1MHz	IEC 60250	3.80
Dielectric strength		IEC 60243-1	53	KV/mm
Volume resistivity		IEC 60093	1E+16	ohms·cm
Surface resistivity		IEC 60093	>1.0E+15	ohms
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	M-Scale	ISO 2039-2	55

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.