PC/PBT XENOY™  X2500UV-GY1D562BZDD SABIC INNOVATIVE US

253
  • Unit Price:US$ 3,157 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    53MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:High impact｜No fill
  • Application Areas:Automotive components｜Electronic and electrical components
  • Color:--
  • Grade:Injection grade

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Charpy Notched Impact Strength-30°CISO 179/1eA30 kJ/m²
Charpy Notched Impact Strength23°CISO 179/1eA50 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eU无断裂
Suspended wall beam without notch impact strength-30°CISO 180/1U无断裂
Dart impact23°C,TotalEnergyASTM D376360.0 J
Charpy Notched Impact Strength-30°CISO 179/1eA30 kJ/m²
Charpy Notched Impact Strength23°CISO 179/1eA50 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eU无断裂
Suspended wall beam without notch impact strength-30°CISO 180/1U无断裂
flammabilityTest ConditionTest MethodTest Result
Burning wire flammability index2.7mmIEC 60695-2-12750 °C
UL flame retardant rating1.5mmUL 94HB
mechanical propertiesTest ConditionTest MethodTest Result
tensile strengthBreak5ASTM D63855.0 Mpa
tensile strengthBreakISO 527-2/5056.0 Mpa
elongationYieldASTMD6385.0 %
elongationYield5ASTM D6385.0 %
elongationBreakASTM D638100 %
elongationBreak5ASTM D63880 %
elongationBreakISO 527-2/5070 %
Bending modulus--ASTM D7902100 Mpa
Bending modulus50.0mmSpan6ASTM D7902150 Mpa
Bending modulus--7ISO 1782150 Mpa
Tensile modulus--4ASTM D6382200 Mpa
Tensile modulus--ISO 527-2/12200 Mpa
tensile strengthYieldASTM D63853.0 Mpa
tensile strengthYield5ASTM D63856.0 Mpa
tensile strengthYieldISO 527-2/5057.0 Mpa
bending strength--ASTM D79079.0 Mpa
bending strength--7,8ISO 17880.0 Mpa
bending strengthYield,50.0mmSpan6ASTM D79079.0 Mpa
Taber abraser1000Cycles,1000g,CS-17WheelInternal Method20.0 mg
Tensile modulus--3ASTM D6382200 Mpa
tensile strengthYield4ASTM D63856.0 Mpa
tensile strengthBreak4ASTM D63855.0 Mpa
elongationYield4ASTM D6385.0 %
elongationBreak4ASTM D63880 %
Bending modulus50.0mmSpan5ASTM D7902150 Mpa
Bending modulus--6ISO 1782150 Mpa
bending strength--6,7ISO 17880.0 Mpa
bending strengthYield,50.0mmSpan5ASTM D79079.0 Mpa
thermal performanceTest ConditionTest MethodTest Result
Hot deformation temperature0.45MPa,Unannealed,64.0mmSpan11ISO 75-2/Bf126 °C
Hot deformation temperature1.8MPa,Unannealed,3.20mmASTM D648108 °C
Hot deformation temperature1.8MPa,Unannealed,64.0mmSpan11ISO 75-2/Af108 °C
Vicat softening temperature--ASTMD152512135 °C
Vicat softening temperature--ISO 306/A50145 °C
Vicat softening temperature--ISO 306/B120136 °C
Ball Pressure Test125°CIEC 60695-10-2通过
Linear coefficient of thermal expansionMD:-40to40°CASTME8318E-05 cm/cm/°C
Linear coefficient of thermal expansionMD:23to80°CISO 11359-28.2E-05 cm/cm/°C
Linear coefficient of thermal expansionTD:-40to40°CASTME8318.5E-05 cm/cm/°C
Linear coefficient of thermal expansionTD:23to80°CISO 11359-28.7E-05 cm/cm/°C
thermal conductivityISO 83020.18 W/m/K
Hot deformation temperature1.8MPa,Unannealed,64.0mmSpan10ISO 75-2/Af108 °C
Vicat softening temperature--ASTMD152511135 °C
Hot deformation temperature0.45MPa,Unannealed,64.0mmSpan10ISO 75-2/Bf126 °C
Physical propertiesTest ConditionTest MethodTest Result
melt mass-flow rate265°C/2.16kgASTM D12389.0 g/10min
Melt Volume Flow Rate (MVR)265°C/1.2kgISO 11334.00 cm3/10min
Shrinkage rateMD3Internal Method0.50-0.80 %
Shrinkage rateMD:3.20mmInternal Method0.50-0.80 %
Shrinkage rateTD3Internal Method0.50-0.80 %
Water absorption rateSaturation,23°CISO 620.70 %
Water absorption rateEquilibrium,23°C,50%RHISO 620.20 %
Shrinkage rateMD2Internal Method0.50-0.80 %
Shrinkage rateTD2Internal Method0.50-0.80 %
Electrical performanceTest ConditionTest MethodTest Result
Surface resistivityIEC 60093>1.0E+15 ohms
Volume resistivityIEC 60093>1.0E+14 ohms·cm
Dielectric strength3.20mm,in OilIEC 60243-117 KV/mm
Relative permittivity50HzIEC 602503.30
Relative permittivity60HzIEC 602503.30
Relative permittivity1MHzIEC 602503.10
Dissipation factor50HzIEC 602502E-03
Dissipation factor60HzIEC 602502E-03
Dissipation factor1MHzIEC 602500.020
hardnessTest ConditionTest MethodTest Result
Ball Pressure TestH358/30ISO 2039-195.0 Mpa
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.