PA66 Ultramid® 8233GHS BK102 BASF GERMANY

305

Unit Price:US$ 3,240 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
69MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Thermal stability｜High impact resistance
Application Areas:Electrical applications｜Industrial machinery
Color:--
Grade:--

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179	65	kJ/m²
Dart impact	23°C	Internal Method	4.07	J
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	3.0mm	UL 94	HB
	UL flame retardant rating	1.5mm	UL 94	HB
	UL flame retardant rating	UL flame retardant rating	0.60mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus	-40°C	ISO 527-2	10300	Mpa
bending strength	23°C	ASTM D790	280	Mpa
bending strength	bending strength	23°C	ISO 178	245	Mpa
Tensile modulus	23°C	ISO 527-2	10200	Mpa
tensile strength	Break,23°C	ISO 527-2	170	Mpa
tensile strength	tensile strength	Break,80°C	ISO 527-2	90.0	Mpa
Tensile modulus	80°C	ISO 527-2	4820	Mpa
	Tensile modulus	120°C	ISO 527-2	4010	Mpa
	Tensile modulus	Tensile modulus	150°C	ISO 527-2	3560	Mpa
tensile strength	Break,-40°C	ASTM D638	230	Mpa
	tensile strength	Break,23°C	ASTM D638	180	Mpa
		tensile strength	Break,80°C	ASTM D638	90.0	Mpa
			tensile strength	Break,121°C	ASTM D638	70.0	Mpa
				tensile strength	Break,-40°C	ISO 527-2	230	Mpa
					tensile strength	Break,120°C	ISO 527-2	70.0	Mpa
					tensile strength	tensile strength	Break,150°C	ISO 527-2	60.0	Mpa
elongation	Break,-40°C	ASTM D638	3.0	%
	elongation	Break,23°C	ASTM D638	3.5	%
		elongation	Break,80°C	ASTM D638	7.0	%
		elongation	elongation	Break,121°C	ASTM D638	7.0	%
Tensile strain	Break,23°C	ISO 527-2	3.0	%
Bending modulus	23°C	ASTM D790	8990	Mpa
Bending modulus	Bending modulus	23°C	ISO 178	8500	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
RTI Str	1.5mm	UL 746	140	°C
RTI Str	RTI Str	0.71mm	UL 746	130	°C
RTI Imp	3.0mm	UL 746	120	°C
	RTI Imp	1.5mm	UL 746	115	°C
	RTI Imp	RTI Imp	0.71mm	UL 746	115	°C
Linear coefficient of thermal expansion	MD	ASTME831	3.8E-05	cm/cm/°C
Melting temperature		ISO 3146	220	°C
Melting temperature	Melting temperature		ASTM D3418	220	°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	205	°C
RTI Str	3.0mm	UL 746	140	°C
RTI Elec	3.0mm	UL 746	140	°C
	RTI Elec	1.5mm	UL 746	140	°C
	RTI Elec	RTI Elec	0.71mm	UL 746	130	°C
Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	208	°C
	Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	218	°C
	Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	215	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	1.8	%
	Water absorption rate	Equilibrium,50%RH	ASTM D570	1.8	%
		Water absorption rate	Saturation,23°C	ISO 62	6.4	%
			Water absorption rate	Saturation	ASTM D570	6.4	%
				Water absorption rate	23°C,24hr	ISO 62	1.1	%
				Water absorption rate	Water absorption rate	24hr	ASTM D570	1.1	%
Shrinkage rate	MD：3.18mm		0.30	%
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale	ASTM D785	121

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PA66 Ultramid® 8233GHS BK102 BASF GERMANY

Material Description

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index