PPS Xytron™ Polyphenylene Sulphide G4010E BK001 DSM HOLAND
192
- Unit Price:US$ 5,034 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 280 °C | |
| Linear coefficient of thermal expansion | 流动 3 | ISO 11359-2 | 1.1E-5 cm/cm/°C |
| 流动 | ISO 11359-2 | 1.5E-5 cm/cm/°C | |
| 横向 | ISO 11359-2 | 5.5E-5 cm/cm/°C | |
| 横向 3 | ISO 11359-2 | 1.1E-4 cm/cm/°C |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 65 kJ/m² |
| 23°C | ISO 179/1eU | 55 kJ/m² |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| shrinkage rate | 横向流量 | ISO 294-4 | 0.50 % |
| 流量 | ISO 294-4 | 0.20 % | |
| Water absorption rate | 饱和, 23°C | ISO 62 | 0.020 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| volume resistivity | IEC 60093 | > 1.0E+15 ohms·cm | |
| dielectric strength | IEC 60243-1 | 33 KV/mm | |
| relative permittivity | 5.00 GHz | IEC 60250 | 3.80 |
| Dissipation Factor | 5.00 GHz | IEC 60250 | 5.5E-3 |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 3 |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | -- | ISO 527-2 | 12000 Mpa |
| 120°C | ISO 527-2 | 6100 Mpa | |
| 160°C | ISO 527-2 | 3900 Mpa | |
| 200°C | ISO 527-2 | 3000 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 160 Mpa |
| 断裂, 120°C | ISO 527-2 | 65.0 Mpa | |
| 断裂, 160°C | ISO 527-2 | 50.0 Mpa | |
| 断裂, 200°C | ISO 527-2 | 40.0 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 2.4 % |
| 断裂, 120°C | ISO 527-2 | 3.9 % | |
| 断裂, 160°C | ISO 527-2 | 4.4 % | |
| 断裂, 200°C | ISO 527-2 | 4.5 % | |
| flexural modulus | -- | ISO 178 | 10000 Mpa |
| 120°C | ISO 178 | 8500 Mpa | |
| 160°C | ISO 178 | 4600 Mpa | |
| 200°C | ISO 178 | 3100 Mpa | |
| bending strength | ISO 178 | 230 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.