PC TARFLON™ RY2200 IDEMITSU JAPAN

246

Unit Price:US$ 2,934 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
40MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Flame retardant
Application Areas:Automotive Applications
Color:--
Grade:Halogen-free flame retardant grade

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result
transmissivity		ISO 13468-1	85.0to89.0 %

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	3.0mm	UL 94	V-0

mechanical properties	Test Condition	Test Method	Test Result
Bending modulus		ISO 178	2300 Mpa
bending strength		ISO 178	90 Mpa
Charpy Notched Impact Strength		ISO 179	80 kJ/m²
bending strength		ISO 178	90.0 Mpa
Bending modulus		ISO 178	2300 Mpa
Nominal tensile fracture strain		ISO 527-2	95 %
tensile strength	Yield	ISO 527-2	65.0 Mpa
Elongation at Break		ISO 527-2	95 %
tensile strength	Yield	ISO 527-2	65 Mpa
Rockwell hardness	R -Sale	ISO 2039-2	120
Rockwell hardness	Rockwell hardness	M -Sale	ISO 2039-2	50

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	125 °C
Linear coefficient of thermal expansion		ISO 11359-2	0.000065 cm/cm/℃
UL flame retardant rating	3.00 mm	UL 94	V-0
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	125 °C
Linear coefficient of thermal expansion	MD	ISO 11359-2	6.5E-05 cm/cm/°C
RTI Elec	1.5mm	UL 746	130 °C
RTI Imp	1.5mm	UL 746	125 °C
RTI Str	1.5mm	UL 746	130 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.23 %
Shrinkage rate	MD:2.00mm	Internal Method	0.50-0.70 %
Shrinkage rate	Shrinkage rate	TD:2.00mm	Internal Method	0.50-0.70 %
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	12.0 cm3/10min
Water absorption rate	Equilibrium,23℃, 50% RH	ISO 62	0.23 %
Shrinkage rate	MD: 2.00 mm	Internal Method	0.5-0.7 %
Shrinkage rate	Shrinkage rate	TD	Internal Method	0.5-0.7 %
Melt Volume Flow Rate (MVR)	MVR	ISO 1133	12 cm3/10min

Electrical performance	Test Condition	Test Method	Test Result
Dielectric constant	1MHz	IEC 60250	2.85
Dielectric strength		IEC 60243-1	30 KV/mm
Dielectric strength	Dielectric strength		IEC 60243-1	30 KV/mm
Arc resistance		ASTM D495	110 sec
Dielectric constant	1 MHz	IEC 60250	2.85

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	M-Sale	ISO 2039-2	50
Rockwell hardness	Rockwell hardness	R-Sale	ISO 2039-2	120

Supplementary Information	Test Condition	Test Method	Test Result
ISO Shortcut			>PC<

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.