PC EMERGE™ 8600-10 WC880054 STYRON TAIWAN
288
- Unit Price:US$ 2,226 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:31MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Flame retardant
- Application Areas:Electrical appliances
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | R级,3.20mm,注塑 | ASTM D785 | 123 |
| R计秤,4.00mm | ISO 2039-2 | 123 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火 | ASTMD648 | 139 °C |
| 1.8MPa,未退火 | ASTM D648 | 127 °C | |
| 1.8MPa,未退火 | ISO 75-2/A | 125 °C | |
| vicat | -- | ASTM D15256 | 149 °C |
| -- | ISO 306/A120 | 150 °C | |
| -- | ISO 306/B50 | 144 °C | |
| Ball pressure temperature | IEC 60335-1 | >125 °C | |
| Linear coefficient of thermal expansion | MD：-22到85°C | ASTM D696 | 6.5E-05 cm/cm/°C |
| RTI Elec | UL 746 | 125 °C | |
| RTI Imp | UL 746 | 125 °C | |
| RTI | UL 746 | 125 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 1.6mm | UL 94 | V-0 |
| Hot filament ignition temperature | 2.0mm | IEC 60695-2-13 | 960 °C |
| Limiting Oxygen Index | ASTMD2863 | 35 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dart impact | 23°C,3.20mm,总能量 | ASTM D3763 | 58.8 J |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | 300°C/1.2kg | ASTMD1238 | 10 g/10min |
| shrinkage rate | MD | ASTM D955 | 0.50-0.70 % |
| MD | ISO 294-4 | 0.50-0.70 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| flexural modulus | 4.00mm,注塑4 | ISO 178 | 2400 Mpa |
| bending strength | 3.20mm,注塑 | ASTM D790 | 93.8 Mpa |
| 4.00mm,注塑4 | ISO 178 | 94.0 Mpa | |
| Tensile modulus | 3.20mm,注塑 | ASTM D638 | 2210 Mpa |
| 4.00mm,注塑 | ISO 527-2/50 | 2200 Mpa | |
| tensile strength | 屈服,3.20mm,注塑3 | ASTM D638 | 60.0 Mpa |
| 屈服,4.00mm,注塑 | ISO 527-2/50 | 60.0 Mpa | |
| 断裂,3.20mm,注塑 | ASTM D638 | 57.9 Mpa | |
| 断裂,4.00mm,注塑 | ISO 527-2/50 | 58.0 Mpa | |
| elongation | 屈服,3.20mm,注塑 | ASTM D638 | 6.2 % |
| 屈服,4.00mm,注塑 | ISO 527-2/50 | 6.0 % | |
| 断裂,3.20mm,注塑 | ASTM D638 | 110 % | |
| 断裂,4.00mm,注塑 | ISO 527-2/50 | 110 % | |
| flexural modulus | 3.20mm,注塑 | ASTM D790 | 2400 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.