'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PBT CELANEX® 2300GV3/20 CELANESE USA
290
- Unit Price:US$ 4,340 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :Guangzhou port, China
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
+86 ********View
For more details, please contact the supplier!
Material Description
- Material Properties:High gloss
- Application Areas:Electronic and electrical accessories｜Automotive sector
- Color:--
- Grade:--
Technical Data Sheet
| Filling analysis | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| ThermalConductivityofMelt | Internal Method | 0.16 | W/m/K | |
| SpecificHeatCapacity of Melt | Internal Method | 1840 | J/kg/°C | |
| Density of Melt | Internal Method | 1.230 | g/cm³ | |
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 43 | kJ/m² |
| 23°C | ISO 179/1eU | 46 | kJ/m² | |
| -30°C | ISO 179/1eU | 34 | kJ/m² | |
| 23°C | ISO 179/1eU | 34 | kJ/m² | |
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| Extreme Oxygen Index | ISO 4589-2 | 20 | % | |
| UL flame retardant rating | 1.5mm | UL 94 | HB | |
| 1.2mm | UL 94 | HB | ||
| 0.8mm | UL 94 | HB | ||
| 1.6mm | UL 94 | HB | ||
| Extreme Oxygen Index | ISO 4589-2 | 21 | % | |
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| bending strength | 23°C | ISO 178 | 170 | Mpa |
| Tensile creep modulus | 1000hr | ISO 899-1 | 4800 | Mpa |
| 1hr | ISO 899-1 | 6200 | Mpa | |
| Tensile strain | Break | ISO 527-2/1A/5 | 3.0 | % |
| tensile strength | Break | ISO 527-2/1A/5 | 125 | Mpa |
| Tensile modulus | ISO 527-2/1A/1 | 7400 | Mpa | |
| ISO 527-2/1A/1 | 3500 | Mpa | ||
| tensile strength | Break | ISO 527-2/1A/5 | 50.0 | Mpa |
| Tensile strain | Break | ISO 527-2/1A/5 | 4.0 | % |
| Tensile creep modulus | 1hr | ISO 899-1 | 3500 | Mpa |
| 1000hr | ISO 899-1 | 2400 | Mpa | |
| bending strength | 23°C | ISO 178 | 86.0 | Mpa |
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 3.5E-05 | cm/cm/°C |
| Vicat softening temperature | ISO 306/B50 | 215 | °C | |
| Hot deformation temperature | 8.0MPa,Unannealed | ISO 75-2/C | 100 | °C |
| 1.8MPa,Unannealed | ISO 75-2/A | 195 | °C | |
| 0.45MPa,Unannealed | ISO 75-2/B | 220 | °C | |
| 0.45MPa,Unannealed | ISO 75-2/B | 180 | °C | |
| 1.8MPa,Unannealed | ISO 75-2/A | 70.0 | °C | |
| Vicat softening temperature | ISO 306/B50 | 190 | °C | |
| Melting temperature | ISO 11357-3 | 225 | °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.1E-04 | cm/cm/°C |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| Melt Volume Flow Rate (MVR) | 250°C/2.16kg | ISO 1133 | 14.0 | cm3/10min |
| Shrinkage rate | TD | ISO 294-4 | 1.0-1.3 | % |
| MD | ISO 294-4 | 0.40-0.50 | % | |
| Water absorption rate | Equilibrium,23°C,50%RH | ISO 62 | 0.15 | % |
| Melt Volume Flow Rate (MVR) | 250°C/2.16kg | ISO 1133 | 20.0 | cm3/10min |
| Water absorption rate | Equilibrium,23°C,50%RH | ISO 62 | 0.20 | % |
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| Dissipation factor | 1MHz | IEC 60250 | 0.019 | |
| 100Hz | IEC 60250 | 1.6E-03 | ||
| Relative permittivity | 1MHz | IEC 60250 | 4.10 | |
| 100Hz | IEC 60250 | 4.20 | ||
| Dielectric strength | IEC 60243-1 | 31 | KV/mm | |
| IEC 60243-1 | 26 | KV/mm | ||
| Relative permittivity | 100Hz | IEC 60250 | 4.40 | |
| 1MHz | IEC 60250 | 4.20 | ||
| Dissipation factor | 100Hz | IEC 60250 | 8.5E-03 | |
| 1MHz | IEC 60250 | 0.018 | ||
| Surface resistivity | IEC 60093 | >1.0E+15 | ohms | |
| Volume resistivity | IEC 60093 | >1.0E+15 | ohms·cm |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.