TPV 3135N DSM HOLAND
232
- Unit Price:US$ 3,532 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Heat resistant grade
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shore hardness | 邵氏A,5秒,挤塑 | ASTM D2240 | 38 |
| 邵氏A,5秒,挤塑 | ISO 868 | 38 | |
| 邵氏A,5秒,注塑 | ASTM D2240 | 43 | |
| 邵氏A,5秒,注塑 | ISO 868 | 43 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| RTI Elec | UL 746 | 50.0 °C | |
| RTI Imp | UL 746 | 50.0 °C | |
| RTI Str | UL 746 | 50.0 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ApparentShearViscosity-Capillary,@206/s | 200°C | ASTM D3835 | 270 Pa·s |
| 200°C | ISO 11443 | 270 Pa·s |
| elastomer | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | 横向流量:100%应变 | ASTM D412 | 1.10 Mpa |
| 横向流量:100%应变 | ISO 37 | 1.10 Mpa | |
| 流量:100%应变 | ASTM D412 | 2.10 Mpa | |
| 流量:100%应变 | ISO 37 | 2.10 Mpa | |
| 断裂 | ASTM D412 | 4.00 Mpa | |
| 断裂 | ISO 37 | 4.00 Mpa | |
| 流量:断裂 | ASTM D412 | 2.20 Mpa | |
| 流量:断裂 | ISO 37 | 2.20 Mpa | |
| elongation | 断裂 | ASTM D412 | 600 % |
| 断裂 | ISO 37 | 600 % | |
| 流量:断裂 | ISO 37 | 200 % | |
| 流量:断裂 | ASTM D412 | 200 % | |
| tear strength | -横向流量 | ASTM D624 | 15 kN/m |
| --2，横向流量 | ISO 34-1 | 15 kN/m | |
| compression set | 23°C,22hr | ASTM D395 | 15 % |
| 23°C,22hr | ISO 815 | 15 % | |
| 70°C,22hr | ASTM D395 | 30 % | |
| 70°C,22hr | ISO 815 | 30 % | |
| 125°C,70hr | ASTM D395 | 52 % | |
| 125°C,70hr | ISO 815 | 52 % |
| aging | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Change rate of tensile strength in air | 100%应变135°C,1000hr，横向 | ISO 188 | 4.0 % |
| 150°C,168hr，横向 | ASTM D573 | 4.0 % | |
| 150°C,168hr，横向 | ISO 188 | 4.0 % | |
| 100%应变150°C,168hr，横向 | ASTM D573 | 11 % | |
| 100%应变150°C,168hr，横向 | ISO 188 | 11 % | |
| Tensile stress change rate | 135°C,1000hr，断裂 | ASTM D573 | -2.0 % |
| 135°C,1000hr，断裂 | ISO 188 | -2.0 % | |
| 150°C,168hr，断裂 | ISO 188 | 1.0 % | |
| 150°C,168hr，断裂 | ASTM D573 | 1.0 % | |
| Change rate of hardness (Shore) in the air | 邵氏A,135°C,1000hr | ASTM D573 | -1.0 |
| 邵氏A,135°C,1000hr | ISO 188 | -1.0 | |
| 邵氏A,150°C,168hr | ISO 188 | 1.0 | |
| 邵氏A,150°C,168hr | ASTM D573 | 1.0 | |
| volume change | 125°C,70hr,inIRM903Oil | ASTM D471 | 150 % |
| 125°C,70hr,inIRM903Oil | ISO 1817 | 150 % | |
| Change rate of tensile strength in air | 135°C,1000hr，横向 | ASTM D573 | 0.0 % |
| 135°C,1000hr，横向 | ISO 188 | 0.0 % | |
| 100%应变135°C,1000hr，横向 | ASTM D573 | 4.0 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.