'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PBT Crastin® SK601 BK851 DUPONT TAIWAN
363
- Unit Price:US$ 2,950 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:30MT
- Delivery Terms:FOB
- Port of Loading :Kaoshiung port, China
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
+86 ********View
For more details, please contact the supplier!
Material Description
- Material Properties:Glass fiber reinforced｜Filler: Glass fiber reinforced material｜Good strength (glass fiber reinforced｜Good strength (glass fiber reinforced｜20%｜20%｜Filler by weight｜20%｜20%｜Filler by weight
- Application Areas:Automotive Applications｜Electronic and electrical components｜Industrial applications｜Automotive Applications｜Industrial applications｜Automotive Applications
- Color:--
- Grade:Enhanced level
Technical Data Sheet
| Other performance | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| Extreme Oxygen Index | ISO 4589-1 | 19 | % | |
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 9.0 | kJ/m² |
| 23°C | ISO 179/1eA | 8.0 | kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 55 | kJ/m² |
| 23°C | ISO 179/1eU | 60 | kJ/m² | |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 8.0 | kJ/m² |
| 23°C | ISO 180/1A | 9.0 | kJ/m² | |
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 60 | kJ/m² |
| 23°C | ISO 180/1U | 60 | kJ/m² | |
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| Burning rate | 1.00mm | ISO 3795 | 28 | mm/min |
| UL flame retardant rating | 0.75mm | UL 94 | HB | |
| 1.5mm | UL 94 | HB | ||
| 0.75mm | IEC 60695-11-10,-20 | HB | ||
| 1.5mm | IEC 60695-11-10,-20 | HB | ||
| Extreme Oxygen Index | ISO 4589-2 | 19 | % | |
| FMVSS flammability | FMVSS302 | B | ||
| Fogging-G-value | condensate)4 | ISO 6452 | 1E-04 | g |
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| Impact strength of simply supported beam without notch | -30℃, Type 1, Edgewise | ISO 179 | 54 | KJ/m |
| Tensile creep modulus | 1000h | ISO 899-1 | 5600 | MPa |
| 1h | ISO 899-1 | 7200 | MPa | |
| Impact strength of cantilever beam gap | 23 ℃, Type 1, Notch A | ISO 180 | 8 | KJ/m |
| Suspended wall beam without notch impact strength | 23 ℃, Type 1 | ISO 180 | 44 | KJ/m |
| bending strength | 23℃ | ISO 178 | 180 | MPa |
| Bending modulus | 23℃ | ISO 178 | 6200 | MPa |
| Tensile modulus | 23℃ | ISO 527-1 | 7400 | MPa |
| Tensile strain | 23℃，Break | ISO 527-1 | 3.2 | % |
| Tensile stress | 23℃，Break | ISO 527-1 | 120 | MPa |
| Charpy Notched Impact Strength | 23℃, Type 1, Edgewise, Notch A | ISO 179 | 7.5 | KJ/m |
| Impact strength of simply supported beam without notch | 23 ℃, Type 1, Edgewise | ISO 179 | 56 | KJ/m |
| Charpy Notched Impact Strength | -30 ℃, Type 1, Edgewise, Notch A | ISO 179 | 9.8 | KJ/m |
| Bending modulus | ISO 178 | 6500 | Mpa | |
| bending strength | ISO 178 | 180 | Mpa | |
| Tensile modulus | ISO 527-2 | 7000 | Mpa | |
| tensile strength | Break | ISO 527-2 | 120 | Mpa |
| Tensile strain | Break | ISO 527-2 | 3.2 | % |
| Tensile creep modulus | 1hr | ISO 899-1 | 7200 | Mpa |
| 1000hr | ISO 899-1 | 5600 | Mpa | |
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| Melting temperature | ISO 3146 | 225 | ℃ | |
| UL flame retardant rating | 3.00 mm | UL 94 | HB | |
| 1.50 mm | UL 94 | HB | ||
| 0.750 mm | UL 94 | HB | ||
| Hot deformation temperature | 1.80 Mpa，Unannealed | ISO 75B-1 | 204 | ℃ |
| 0.45 Mpa，Unannealed | ISO 75B-1 | 220 | ℃ | |
| Linear coefficient of thermal expansion | 垂直Flow，23 to 55℃(73 to 130°F) | ISO 11359-1 | 0.000040 | cm/cm/℃ |
| 平行Flow，23 to 55℃(73 to 130°F) | ISO 11359-1 | 0.000100 | cm/cm/℃ | |
| Hot deformation temperature | 0.45MPa,Unannealed | ISO 75-2/B | 220 | °C |
| 1.8MPa,Unannealed | ISO 75-2/A | 204 | °C | |
| Vicat softening temperature | ISO 306/B50 | 210 | °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 4E-05 | cm/cm/°C |
| Melting temperature | ISO 11357-3 | 224 | °C | |
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 1E-04 | cm/cm/°C |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| density | ISO 1183 | 1.45 | ||
| Shrinkage rate | Flow | ISO 294-4 | 0.35 | % |
| Across Flow | ISO 294-4 | 1.0 | % | |
| Water absorption rate | Sat/23C | ISO 62 | 0.4 | % |
| 23C/59RH | ISO 62 | 0.15 | % | |
| Top out temperature | 170 | °C | ||
| MediumDensity | 1.26 | g/cm³ | ||
| SpecificHeatCapacity of Melt | 1860 | J/kg/°C | ||
| density | ISO 1183 | 1.45 | g/cm³ | |
| Shrinkage rate | TD | ISO 294-4 | 1.1 | % |
| MD | ISO 294-4 | 0.30 | % | |
| Water absorption rate | Saturation,23°C,2.00mm | ISO 62 | 0.40 | % |
| Equilibrium,23°C,2.00mm,50%RH | ISO 62 | 0.15 | % | |
| ThermalConductivityofMelt | 0.25 | W/m/K | ||
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| Relative permittivity | 1MHz | IEC 60250 | 3.60 | |
| Dissipation factor | 100Hz | IEC 60250 | 1.2E-03 | |
| 1MHz | IEC 60250 | 0.019 | ||
| Compared to the anti leakage trace index | IEC 60112 | PLC 2 | ||
| Surface resistivity | IEC 60093 | 1E+15 | ohms | |
| Volume resistivity | IEC 60093 | >1.0E+15 | ohms·cm | |
| Dielectric strength | IEC 60243-1 | 29 | KV/mm | |
| Relative permittivity | 100Hz | IEC 60250 | 4.00 | |
| Supplementary Information | Test Condition | Test Method | Test Result | Test Unit |
| EmissionofOrganicCompounds | VDA277 | 140 | µgC/g | |
| Odor | VDA270 | 3.00 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.