EAA PRIMACOR™ 3440 STYRON US

Unit Price:US$ 4,290 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
20MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Transaction Guarantee:

Supplier Information

Guangzhou Hushang Chemical Co., Ltd

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Resistance to stress cracking｜High toughness｜Heat sealing performance
Application Areas:Food service sector｜Soft packaging composite materials Liquid packaging composite materials
Color:--
Grade:Injection grade

Technical Data Sheet

Other performance	Test Condition	Test Method	Test Result	Test Unit
Water vapor permeability	38℃，90% RH	DIN 53122/2	0.41	g·mm/m2/atm/24hr
Starting temperature of heat sealing		Internal Method	85	℃
Basic Performance	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	190℃/2.16kg	ISO 1133	11	g/10min
melt mass-flow rate	melt mass-flow rate	190℃/2.16kg	ASTM D-1238	11	g/10min
Monomer content		Internal Method	9.7	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
elongation	Break,Compression Molded	ASTMD638	600	%
tensile strength	Break,Compression Molded	ASTMD638	17.6	Mpa
tensile strength	tensile strength	Yield,Compression Molded	ASTMD638	7.93	Mpa
Elongation at Break	Compression Molded	ISO 527-2	600	%
Elongation at Break	Elongation at Break	Compression Molded	ASTM D-638	600	%
tensile strength	Compression Molded，Break	ISO 527-2	17.6	MPa
	tensile strength	Compression Molded，Break	ASTM D-638	17.6	MPa
		tensile strength	Yield,Compression Molded	ISO 527-2	7.93	MPa
		tensile strength	tensile strength	Yield,Compression Molded	ASTM D-638	7.93	MPa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Vicat softening temperature		ASTMD1525	81.1	°C
Melting temperature		Internal Method	97.8	°C
Vicat softening temperature		ASTM D-1525	81.1	℃
Melting temperature		Internal Method	97.8	℃
Vicat softening temperature		ISO 306	81.1	℃
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Content of comonomer		Internal Method	9.7	%
melt mass-flow rate	190°C/2.16kg	ASTMD1238	11	g/10min
density		ASTMD792	0.938	g/cm³
	density		ISO 1183	0.938	g/cm³
	density	density		ASTM D-792	0.938	g/cm³
film	Test Condition	Test Method	Test Result	Test Unit
Water vapor permeability	38°C,90%RH	DIN 53122/2	0.41	g·mm/m²/atm/24hr
Initial sealing temperature		Internal Method	85.0	°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Other Prices

Supplier	Unit Price
Shenzhen Hongbang	US$ 1640 /MT
ASIAPLAS	US$ 3240 /MT

Supplier Join

Get App

Top

EAA PRIMACOR™ 3440 STYRON US

Material Description

Technical Data Sheet

Other Prices

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index