PA66

PA66 Zytel® 13T1 BK DUPONT USA

201

Unit Price:US$ 3,746 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
50MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Thermal stability
Application Areas:Automotive interior parts｜Electrical applications
Color:--
Grade:Injection grade

Technical Data Sheet

Basic Performance	Test Condition	Test Method	Test Result
Water absorption rate	23℃,Equilibrium	ISO 62	DAM｜1.6 %
	Water absorption rate	23℃,Equilibrium	ISO 62	50%RH｜- %
		Water absorption rate	23℃,Saturation	ISO 62	DAM｜6 %
		Water absorption rate	Water absorption rate	23℃,Saturation	ISO 62	50%RH｜- %
density			DAM｜1.35 g/ml
density	density			50%RH｜1.35 g/ml

mechanical properties	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	Notched-30℃		DAM｜6.0 kJ/m²
	Charpy Notched Impact Strength	Notched-30℃		50%RH｜5.0 kJ/m²
		Charpy Notched Impact Strength	Unnotched-40℃	ISO 179	DAM｜130 kJ/m²
		Charpy Notched Impact Strength	Charpy Notched Impact Strength	Unnotched-40℃	ISO 179	50%RH｜120 kJ/m²
tensile strength	5mm/min	ISO 527	DAM｜72 Mpa
tensile strength	tensile strength	5mm/min	ISO 527	50%RH｜50 Mpa
Charpy Notched Impact Strength	Notched23℃	ISO 179	DAM｜8.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Notched23℃	ISO 179	50%RH｜13.0 kJ/m²
Rockwell hardness		ISO 2039/2	DAM｜118 Scale R
Rockwell hardness	Rockwell hardness		ISO 2039/2	50%RH｜- Scale R
Charpy Notched Impact Strength	Unnotched23℃	ISO 179	DAM｜NB kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Unnotched23℃	ISO 179	50%RH｜NB kJ/m²
Elongation at Break	5mm/min	ISO 527	DAM｜18 %
Elongation at Break	Elongation at Break	5mm/min	ISO 527	50%RH｜47 %
Impact strength of cantilever beam gap	-30℃	ISO 180	DAM｜4.6 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-30℃	ISO 180	50%RH｜3.7 kJ/m²
Young's modulus	1mm/min		DAM｜4000 Mpa
Young's modulus	Young's modulus	1mm/min		50%RH｜1500 Mpa
Rockwell hardness		ISO 2039/2	DAM｜80 Scale M
Rockwell hardness	Rockwell hardness		ISO 2039/2	50%RH｜- Scale M
Impact strength of cantilever beam gap	23℃	ISO 180	DAM｜10.7 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23℃	ISO 180	50%RH｜13 kJ/m²

thermal performance	Test Condition	Test Method	Test Result
Melting temperature		ISO 1218	255 °C
Melting temperature	Melting temperature		ISO 1218	255 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	Across Flow	ISO 2577	DAM｜1.6 %
	Shrinkage rate	Across Flow	ISO 2577	50%RH｜- %
		Shrinkage rate	Flow	ISO 2577	DAM｜1.4 %
		Shrinkage rate	Shrinkage rate	Flow	ISO 2577	50%RH｜- %

Electrical performance	Test Condition	Test Method	Test Result
Dissipation factor	1MHz	ISO 250	DAM｜200 10-4
	Dissipation factor	1MHz	ISO 250	50%RH｜650 10-4
		Dissipation factor	50Hz	IEC 250	DAM｜100 10-4
		Dissipation factor	Dissipation factor	50Hz	IEC 250	50%RH｜4500 10-4
Dielectric strength		IEC 243	DAM｜35 KV/mm
Dielectric strength	Dielectric strength		IEC 243	50%RH｜- KV/mm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PA66 Zytel® 13T1 BK DUPONT USA

Material Description

Technical Data Sheet Compare

Technical Data Sheet