PC/ABS CYCOLOY™ C1200 WH9B177 SABIC INNOVATIVE NANSHA

383

Unit Price:US$ 2,440 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
29MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High impact resistance｜heat-resisting
Application Areas:Electrical field｜Electronic field｜Automotive interior parts
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Dart impact	23°C,TotalEnergy	ASTM D3763	54.2	J
Dart impact	Dart impact	-30°C,TotalEnergy	ASTM D3763	54.2	J
Impact strength of cantilever beam gap	23°C	ISO 180/1A	49	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-30°C	ISO 180/1A	34	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.2mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength	Yield,50.0mmSpan	ASTM D790	88.3	Mpa
elongation	Yield	ASTM D638	5.0	%
tensile strength	Yield	ISO 527-2/50	55.0	Mpa
tensile strength	tensile strength	Yield	ASTM D638	57.2	Mpa
Tensile modulus		ISO 527-2/1	2370	Mpa
Tensile modulus	Tensile modulus		ASTM D638	2280	Mpa
bending strength		ISO 178	86.0	Mpa
Bending modulus		ISO 178	2250	Mpa
Bending modulus	Bending modulus	50.0mmSpan	ASTM D790	2340	Mpa
Tensile strain	Break	ISO 527-2/50	110	%
elongation	Break	ASTM D638	150	%
Tensile strain	Yield	ISO 527-2/50	4.8	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	7.2E-05	cm/cm/°C
RTI Elec		UL 746	105	°C
Vicat softening temperature		ISO 306/B50	130	°C
Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	110	°C
	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	113	°C
		Hot deformation temperature	0.45MPa,Unannealed,64.0mmSpan	ISO 75-2/Bf	130	°C
		Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	129	°C
RTI Imp		UL 746	80.0	°C
RTI Str		UL 746	105	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	MD：3.20mm	Internal Method	0.50-0.70	%
Melt Volume Flow Rate (MVR)	265°C/5.0kg	ISO 1133	24.0	cm3/10min
melt mass-flow rate	260°C/5.0kg	ASTM D1238	19	g/10min
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Compared to the anti leakage trace index	CTI	UL 746	PLC 2
High arc combustion index	HAI	UL 746	PLC 1
Hot wire ignition	HWI	UL 746	PLC 3

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PC/ABS CYCOLOY™ C1200 WH9B177 SABIC INNOVATIVE NANSHA

Material Description

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index