Material Description
- Material Properties:Thermal stability｜Filler: Glass fiber reinforced material｜30% filler by weight
- Application Areas:Automotive Applications｜Electronic and electrical components
- Color:--
- Grade:Enhanced level
Material Certification
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | R级 | ISO 2039-2 | 121 |
| ball-indentation hardness | H961/30 | ISO 2039-1 | 230 Mpa |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO 75-2/B | 220 °C |
| 1.8MPa,未退火 | ISO 75-2/A | 210 °C | |
| Glass Transition Temperature | ISO 11357-2 | 60.0 °C | |
| vicat | ISO 306/B50 | 215 °C | |
| melting temperature | ISO 11357-3 | 221 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 2.6E-05 cm/cm/°C |
| TD | ISO 11359-2 | 7.5E-05 cm/cm/°C | |
| Effective thermal diffusivity coefficient | 9.1E-08 m²/s |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| burning rate | 1.00mm | ISO 3795 | 50 mm/min |
| UL flame retardant rating | 0.75mm | UL 94 | HB |
| 1.5mm | UL 94 | HB | |
| 0.75mm | IEC 60695-11-10,-20 | HB | |
| 1.5mm | IEC 60695-11-10,-20 | HB | |
| Limiting Oxygen Index | ISO 4589-2 | 21 % | |
| FMVSS flammability | FMVSS302 | B | |
| atomization | F-value(refraction) | ISO 6452 | 95 % |
| G-value(condensate) | ISO 6452 | 1E-04 g |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Emissions of Organic Compounds | VDA277 | 8.50 µgC/g | |
| Odor | VDA270 | 3.50 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 10 kJ/m² |
| 23°C | ISO 179/1eA | 16 kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 80 kJ/m² |
| 23°C | ISO 179/1eU | 100 kJ/m² | |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 10 kJ/m² |
| 23°C | ISO 180/1A | 15 kJ/m² | |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 80 kJ/m² |
| Multi axis Instrumented Impact Energy | 23°C | ISO 6603-2 | 3.50 J |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| MediumDensity | 1.20 g/cm³ | ||
| SpecificHeatCapacity of Melt | 2280 J/kg/°C | ||
| ThermalConductivityofMelt | 0.26 W/m/K | ||
| density | ISO 1183 | 1.36 g/cm³ | |
| Melt volume flow rate | 250°C/5.0kg | ISO 1133 | 15.0 cm3/10min |
| shrinkage rate | TD | ISO 294-4 | 0.60 % |
| MD | ISO 294-4 | 0.20 % | |
| Water absorption rate | 饱和,23°C,2.00mm | ISO 62 | 6.3 % |
| 平衡,23°C,2.00mm,50%RH | ISO 62 | 1.9 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile creep modulus | 1000hr | ISO 899-1 | -- Mpa |
| flexural modulus | ISO 178 | 8500 Mpa | |
| bending strength | ISO 178 | 280 Mpa | |
| Tensile modulus | ISO 527-2 | 9500 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 190 Mpa |
| Tensile strain | 断裂 | ISO 527-2 | 3.5 % |
| Tensile creep modulus | 1hr | ISO 899-1 | -- Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.