PA66 Zytel® FR52G30NH BK756A DUPONT USA
166
- Unit Price:US$ 3,575 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:20.1MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Flame retardant｜Glass fiber reinforced
- Application Areas:Electrical applications｜Automotive Applications｜electrical equipment
- Color:--
- Grade:--
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| RTI Elec | 0.400mm | °C | 140 -- |
| 0.750mm | °C | 140 -- | |
| 1.50mm | °C | 140 -- | |
| 3.00mm | °C | 140 -- | |
| Heat Deflection Temperature | 1.8MPa,未退火 | °C | 281 -- |
| melting temperature | °C | 310 -- | |
| Linear coefficient of thermal expansion | MD | cm/cm/°C | 1.8E-05 -- |
| MD:-40到23°C | cm/cm/°C | 1.8E-05 -- | |
| MD:55到160°C | cm/cm/°C | 1.2E-05 -- | |
| TD | cm/cm/°C | 6.2E-05 -- | |
| TD:-40到23°C | cm/cm/°C | 6E-05 -- | |
| TD:55到160°C | cm/cm/°C | 9.5E-05 -- |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Flammability level | 0.400mm | V-0 -- | |
| 1.50mm | V-0 -- | ||
| Burning wire flammability index | 0.400mm | °C | 960 -- |
| 3.00mm | °C | 960 -- | |
| Hot filament ignition temperature | 0.400mm | °C | 700 -- |
| 3.00mm | °C | 775 -- | |
| Limiting Oxygen Index | % | 37 -- |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | kJ/m² | 40 |
| 23°C | kJ/m² | 45 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| shrinkage rate | TD | % | 1.0 -- |
| MD | % | 0.30 -- |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | V | PLC 0 |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | MPa | 10700 11300 | |
| tensile strength | 断裂 | 145 MPa | |
| Tensile strain | 断裂 | % | 2.1 1.9 |
| flexural modulus | MPa | 9800 10800 | |
| bending strength | 225 MPa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.