ASA/PC

ASA/PC GELOY™ XP4034-BK1041 SABIC INNOVATIVE NANSHA

522

Unit Price:US$ 3,547 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
108MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Thermal stability｜Weather resistance｜Antistatic｜High mobility
Application Areas:Automotive Applications
Color:--
Grade:Injection grade

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result
gloss	60°, 无织构	ASTM D523	94

impact performance	Test Condition	Test Method	Test Result
Dart impact	23°C, Total Energy	ASTM D3763	47.0 J
Dart impact	Dart impact	-30°C, Total Energy	ASTM D3763	30.0 J

mechanical properties	Test Condition	Test Method	Test Result
bending strength	Yield, 50.0 mm Span	ASTM D790	88.0 Mpa
Bending modulus	50.0 mm Span	ASTM D790	2510 Mpa
elongation	Break	ASTM D638	25 %
tensile strength	Yield	ASTM D638	62.0 Mpa

injection	Test Condition	Test Method	Test Result
Spray nozzle temperature			245 to 265 °C
Processing (melt) temperature			260 to 275 °C
Mold temperature			55 to 70 °C
Back pressure			0.300 to 1.00 Mpa
Screw speed			30 to 80 rpm
Exhaust hole depth			0.038 to 0.076 mm
Temperature at the front of the material cylinder			250 to 265 °C
Temperature in the middle of the barrel			245 to 260 °C
Temperature at the rear of the barrel			240 to 255 °C
Suggested injection volume			40 to 80 %
Suggested maximum moisture content			0.040 %
drying time			3.0 to 4.0 hr
drying temperature			95 to 105 °C

thermal performance	Test Condition	Test Method	Test Result
thermal conductivity		ASTM C177	0.25 W/m/K
Linear coefficient of thermal expansion	Across Flow : -20 to 150°C	ASTM E831	7.2E-5 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Flow : -20 to 150°C	ASTM E831	7.2E-5 cm/cm/°C
Hot deformation temperature	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	104 °C
Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	115 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	24 hr	ASTM D570	0.25 %
Shrinkage rate	Across FlowFlow : 3.20 mm	Internal Method	0.50 - 0.70 %
Shrinkage rate	Shrinkage rate	Flow : 3.20 mm	Internal Method	0.50 - 0.70 %
melt mass-flow rate	280°C/3.8 kg	ASTM D1238	24 g/10 min

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale	ASTM D785	110

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.