Material Description

Material Properties:High gloss
Application Areas:Household goods｜Lighting fixtures｜Non specific food applications
Color:--
Grade:--

Technical Data Sheet

other	Test Condition	Test Method	Test Result
purpose			食品容器、小家电
characteristic			食品级、低残单

mechanical properties	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap		ASTM D256/ISO 179	9 kg·cm/cm(J/M)ft·lb/in
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ASTM D256/ISO 179	19 kg·cm/cm(J/M)ft·lb/in
Charpy Notched Impact Strength		ASTM D256/ISO 179	10 kg·cm/cm(J/M)ft·lb/in
Charpy Notched Impact Strength	Charpy Notched Impact Strength		ASTM D256/ISO 179	21 kg·cm/cm(J/M)ft·lb/in
bending strength		ASTM D790/ISO 178	76 kg/cm²(MPa)[Lb/in²]
Bending modulus		ASTM D790/ISO 178	2.2 kg/cm²(MPa)[Lb/in²]
elongation		ASTM D638/ISO 527	30 %
tensile strength		ASTM D638/ISO 527	47 kg/cm²(MPa)[Lb/in²]
Tensile modulus		ASTM D638/ISO 527	34 kg/cm²(MPa)[Lb/in²]

thermal performance	Test Condition	Test Method	Test Result
Vickers softening temperature	1 Kg,50℃/hr	ISO 306	104 °C
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	8.6×10-5 mm/mm.℃
Vicat softening temperature		ASTM D1525/ISO R306	104 ℃（℉）
Hot deformation temperature	HDT	ASTM D648/ISO 75	83 ℃（℉）
	Hot deformation temperature	HDT	ASTM D648/ISO 75	98 ℃（℉）
	Hot deformation temperature	Hot deformation temperature	1.8 MPa Unannealed	ISO 75/A	83 °C
linear expansion coefficient		ISO 11359	8.6 x 10-5
Flame Rating	1.5mm	UL -94	HB

Physical properties	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	23 ℃ Notched	ISO 180/1A	19
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-30℃ Notched		KJ/m2
Charpy Notched Impact Strength	23℃ Notched	ISO 179	21 kJ/m²
Bending modulus of elasticity		ISO 178	2.2 GPa
bending strength		ISO 178	76 Mpa
Shrinkage rate		ASTM D955	0.4-0.7 %
density		ASTM D792/ISO 1183	1.05
Elongation at Break	50 mm/min, break	ISO 527	30 %
Molding shrinkage rate		ISO 294-4	0.4-0.7 %
Melt index	220℃×10KG	ISO 1133	18 ml/10 min
Tensile strength, 50 mm/min, yield		ISO 527	47 Mpa
melt mass-flow rate		ASTM D1238/ISO 1133	18 g/10min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.