Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	230℃/3.8 kg	ISO 1133	0.50 g/10 min
shrinkage rate		内部方法	0.20-0.60 %
Water absorption rate	饱和, 23℃	ISO 62	0.30 %
density		ASTM D792/ISO 1183	1.19
Water absorption rate		ASTM D570/ISO 62	0.3 %

mechanical properties	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength		ISO 179/1eU	24 kJ/m²
Tensile modulus		ISO 527-2/1A/1	3300
tensile strength	断裂	ISO 527-2/1A/5	75.0 Mpa
Tensile strain	断裂	ISO 527-2/1A/5	8.0 %
flexural modulus		ISO 178	3300 Mpa
bending strength		ISO 178	130 Mpa
Charpy Notched Impact Strength		ISO 179/1eA	1.4 kJ/m²
Tensile modulus		ASTM D638/ISO 527	3300(MPa) kg/cm²(MPa)[Lb/in²]
flexural modulus		ASTM D790/ISO 178	3300(MPa) kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	130(MPa) kg/cm²(MPa)[Lb/in²]

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.