Impact strength of simply supported beam without notch
-30°C,Complete Break
ISO 179/1eU
100 kJ/m²
Charpy Notched Impact Strength
23°C,CompleteBreak
ISO 7391
10 kJ/m²
Multi axis Instrumented Impact Energy
-30°C
ISO 6603-2
13.0 J
Impact strength of simply supported beam without notch
23°C,Complete Break
ISO 179/1eU
120 kJ/m²
Multi axis Instrumented Impact Energy
23°C
ISO 6603-2
25.0 J
Impact strength of cantilever beam gap
23°C,CompleteBreak
ISO 7391
10 kJ/m²
Multi axis Instrumented Peak Impact Force
23°C
ISO 6603-2
3600 N
Impact strength of simply supported beam without notch
-60°C,CompleteBreak
ISO 179/1eU
90 kJ/m²
Multi axis Instrumented Peak Impact Force
-30°C
ISO 6603-2
3000 N
flammability
Test Condition
Test Method
Test Result
Needle flame test
MethodF:2.00mm
IEC 60695-11-5
2.0 min
Burning wire flammability index
3.0mm
IEC 60695-2-12
960 °C
SelfIgnition
ASTM D1929
550 °C
Needle flame test
MethodK:2.00mm
IEC 60695-11-5
1.0 min
Needle flame test
MethodF:1.50mm
IEC 60695-11-5
2.0 min
UL flame retardant rating
3.0mm
UL 94
V-0
Hot filament ignition temperature
1.5mm
IEC 60695-2-13
900 °C
Needle flame test
MethodK:3.00mm
IEC 60695-11-5
2.0 min
Burning wire flammability index
0.75mm
IEC 60695-2-12
850 °C
UL flame retardant rating
1.5mm
UL 94
V-2
Hot filament ignition temperature
3.0mm
IEC 60695-2-13
900 °C
Burning rate - US-FMVSS
>1.00mm
ISO 3795
passed
Needle flame test
MethodK:1.50mm
IEC 60695-11-5
1.0 min
Hot filament ignition temperature
0.75mm
IEC 60695-2-13
850 °C
Needle flame test
MethodF:3.00mm
IEC 60695-11-5
2.0 min
Burning wire flammability index
1.5mm
IEC 60695-2-12
960 °C
FlashIgnitionTemperature
ASTM D1929
470 °C
Extreme Oxygen Index
ISO 4589-2
27 %
mechanical properties
Test Condition
Test Method
Test Result
Tensile strain
Yield,23°C
ISO 527-2/5
4.6 %
Bending strain
23°C
ISO 178
5.8 %
Tensile modulus
23°C
ISO 527-2/1
4600 Mpa
Tensile strain
Break,23°C
ISO 527-2/5
12 %
tensile strength
Break,23°C
ISO 527-2/5
45.0 Mpa
tensile strength
Yield,23°C
ISO 527-2/5
64.0 Mpa
bending strength
3.5%Strain,23°C
ISO 178
95.0 Mpa
Bending modulus
23°C
ISO 178
4400 Mpa
bending strength
23°C
ISO 178
105 Mpa
thermal performance
Test Condition
Test Method
Test Result
Linear coefficient of thermal expansion
MD：23to55°C
ISO 11359-2
3.5E-05 cm/cm/°C
RTI Elec
1.5mm
UL 746
80.0 °C
Hot deformation temperature
1.8MPa,Unannealed
ISO 75-2/A
135 °C
Hot deformation temperature
0.45MPa,Unannealed
ISO 75-2/B
141 °C
Vicat softening temperature
--
ISO 306/B120
145 °C
Ball Pressure Test
136°C
IEC 60695-10-2
Pass
Linear coefficient of thermal expansion
TD：23to55°C
ISO 11359-2
6.5E-05 cm/cm/°C
RTI Imp
1.5mm
UL 746
80.0 °C
RTI Str
1.5mm
UL 746
80.0 °C
Vicat softening temperature
--
ISO 306/B50
142 °C
Physical properties
Test Condition
Test Method
Test Result
Melt Volume Flow Rate (MVR)
300°C/1.2kg
ISO 1133
6.00 cm3/10min
Shrinkage rate
TD:2.00mm
ISO 294-4
0.45 %
melt mass-flow rate
300°C/1.2kg
ISO 1133
7.0 g/10min
Water absorption rate
Equilibrium,23°C,50%RH
ISO 62
0.10 %
Shrinkage rate
MD:2.00mm
ISO 294-4
0.45 %
Water absorption rate
Saturation,23°C
ISO 62
0.24 %
Apparent density
ISO 60
0.64 g/cm³
Electrical performance
Test Condition
Test Method
Test Result
Relative permittivity
23°C,1MHz
IEC 60250
3.20
Dissipation factor
23°C,1MHz
IEC 60250
9E-03
Dissipation factor
23°C,100Hz
IEC 60250
1E-03
Compared to the anti leakage trace index
SolutionB
IEC 60112
PLC 4
Relative permittivity
23°C,100Hz
IEC 60250
3.20
Surface resistivity
IEC 60093
1E+16 ohms
Dielectric strength
23°C,1.00mm
IEC 60243-1
38 KV/mm
Volume resistivity
23°C
IEC 60093
1E+16 ohms·cm
Compared to the anti leakage trace index
SolutionA
IEC 60112
PLC 3
hardness
Test Condition
Test Method
Test Result
Ball Pressure Test
ISO 2039-1
129 Mpa
Supplementary Information
Test Condition
Test Method
Test Result
Electrolytic corrosion
23°C
IEC 60426
A1
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)