PBT VALOX™ 420SE0 BK1066 SABIC INNOVATIVE US
439
- Unit Price:US$ 3,523 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:83.8MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
- Material Comparison:PBT LONGLITE® 4830 BK TAIWAN CHANGCHUN
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Glass fiber reinforced｜dimensional stability ｜High rigidity｜high strength｜heat-resisting
- Application Areas:Lawn equipment｜Garden equipment｜Industrial applications｜Automotive External Parts｜Electrical field｜Electronic field｜Architectural application field｜Outdoor applications｜Electrical appliances｜Engine hood parts｜Medical supplies｜Nursing supplies｜Plastic bag｜Automotive interior parts｜Casters｜Household goods｜Petroleum Applications｜Natural gas supplies｜sporting goods｜Textile application｜Lighting applications
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 119 |
| R级 | ISO 2039-2 | 119 | |
| ball-indentation hardness | H358/30 | ISO 2039-1 | 118 Mpa |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,Unannealed,100mmSpan | ISO 75-2/Be | 220 °C |
| 1.8MPa,未退火,3.20mm | ASTM D648 | 200 °C | |
| 1.8MPa,未退火,100mm跨距9 | ISO 75-2/Ae | 195 °C | |
| 1.8MPa,未退火,64.0mm跨距10 | ISO 75-2/Af | 200 °C | |
| vicat | ASTM D152511 | 200 °C | |
| -- | ISO 306/A50 | 220 °C | |
| -- | ISO 306/B50 | 200 °C | |
| -- | ISO 306/B120 | 200 °C | |
| ball-indentation hardness | 125°C | IEC 60695-10-2 | Pass |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 2.5E-05 cm/cm/°C |
| MD：-40to40°C | ISO 11359-2 | 2.5E-05 cm/cm/°C | |
| MD：23到80°C | ISO 11359-2 | 2.5E-05 cm/cm/°C | |
| TD：-40到40°C | ASTME831 | 8.9E-05 cm/cm/°C | |
| TD：-40to40°C | ISO 11359-2 | 8.9E-05 cm/cm/°C | |
| TD：23到80°C | ISO 11359-2 | 1.2E-04 cm/cm/°C | |
| thermal conductivity | ISO 8302 | 0.25 W/m/K | |
| RTI Elec | UL 746 | 130 °C | |
| RTI Imp | UL 746 | 130 °C | |
| RTI Str | UL 746 | 140 °C | |
| Heat Deflection Temperature | 0.45MPa,未退火,3.20mm | ASTM D648 | 212 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Limiting Oxygen Index | ISO 4589-2 | 32 % | |
| UL flame retardant rating | 0.40mm | UL 94 | V-2 |
| 0.71mm | UL 94 | V-0 | |
| 2.0mm | UL 94 | 5VA | |
| Burning wire flammability index | 1.0mm | IEC 60695-2-12 | 960 °C |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 6.0 kJ/m² |
| 23°C | ISO 179/1eA | 7.0 kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 50 kJ/m² |
| 23°C | ISO 179/1eU | 50 kJ/m² | |
| Impact strength of cantilever beam gap | -30°C | ASTM D256 | 57 J/m |
| 23°C | ASTM D256 | 60 J/m | |
| -30°C | ISO 180/1A | 6.0 kJ/m² | |
| 23°C | ISO 180/1A | 7.0 kJ/m² | |
| 23°C | ASTM D4812 | 620 J/m | |
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 45 kJ/m² |
| 23°C | ISO 180/1U | 45 kJ/m² | |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 5.00 J |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 3 |
| -- | IEC 60112 | PLC 3 | |
| 解决方案B | IEC 60112 | PLC 4 | |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 0 |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 4 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 2 |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| volume resistivity | ASTM D257 | >1.0E+15 ohms·cm | |
| IEC 60093 | >1.0E+15 ohms·cm | ||
| dielectric strength | 1.60mm,在油中 | ASTM D149 | 24 KV/mm |
| 3.20mm,inAir | ASTM D149 | 19 KV/mm | |
| 0.800mm,在油中 | IEC 60243-1 | 23 KV/mm | |
| 1.60mm,在油中 | IEC 60243-1 | 22 KV/mm | |
| 3.20mm,在油中 | IEC 60243-1 | 16 KV/mm | |
| dielectric constant | 100Hz | ASTM D150 | 3.80 |
| 1MHz | ASTM D150 | 3.70 | |
| relative permittivity | 50Hz | IEC 60250 | 3.30 |
| 60Hz | IEC 60250 | 3.30 | |
| 100Hz | IEC 60250 | 3.80 | |
| 1MHz | IEC 60250 | 3.30 | |
| Dissipation Factor | 100Hz | ASTM D150 | 2E-03 |
| 1MHz | ASTM D150 | 0.020 | |
| 50Hz | IEC 60250 | 1E-03 | |
| 60Hz | IEC 60250 | 1E-03 | |
| 100Hz | IEC 60250 | 2E-03 | |
| 1MHz | IEC 60250 | 0.010 | |
| arc resistance | ASTM D495 | PLC6 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792 | 1.63 g/cm³ | |
| Specific volume | ASTM D792 | 0.610 cm³/g | |
| density | ISO 1183 | 1.63 g/cm³ | |
| melt mass-flow rate | 250°C/5.0kg | ASTM D1238 | 42 g/10min |
| Melt volume flow rate | 250°C/5.0kg | ISO 1133 | 29.0 cm3/10min |
| shrinkage rate | MD：--2 | 内部方法 | 0.10-0.50 % |
| MD：3.20mm | 内部方法 | 0.50-0.70 % | |
| TD：--2 | 内部方法 | 0.40-0.80 % | |
| TD：3.20mm | 内部方法 | 0.50-1.0 % | |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.090 % |
| 平衡,23°C,50%RH | ISO 62 | 0.070 % | |
| Outdoor applicability | UL 746C | f2 |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| flexural modulus | ISO 178 | 9500 Mpa | |
| bending strength | ISO 178 | 180 Mpa | |
| Break,50.0mmSpan | ASTM D790 | 186 Mpa | |
| Taber abraser | 1000Cycles,1000g,CS-17转轮 | 内部方法 | 22.0 mg |
| Tensile modulus | ISO 527-2/1 | 10000 Mpa | |
| tensile strength | 屈服 | ASTM D638 | 120 Mpa |
| 屈服 | ISO 527-2/5 | 120 Mpa | |
| Break | ASTM D638 | 120 Mpa | |
| 断裂 | ISO 527-2/5 | 120 Mpa | |
| elongation | 屈服 | ASTM D638 | 2.0 % |
| Tensile strain | 屈服 | ISO 527-2/5 | 1.9 % |
| elongation | 断裂 | ASTM D638 | 2.0 % |
| Tensile strain | 断裂 | ISO 527-2/5 | 1.9 % |
| flexural modulus | 50.0mmSpan | ASTM D790 | 9800 Mpa |
| Tensile modulus | ASTM D638 | 12000 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.