'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PC LEXAN™ EXL1414 WH9A320 SABIC INNOVATIVE NANSHA
11
- Unit Price:US$ 5,520 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:15MT
- Delivery Terms:FOB
- Port of Loading :Guangzhou port, China
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Transaction Guarantee:
Supplier Information
Dongguan Ruiying Plastic Co., Ltd
+86 755 ********View
serv********View
+86 ********View
For more details, please contact the supplier!
Material Description
- Material Properties:Processability｜Moderate liquidity｜Ductility｜copolymer｜Good demolding performance
- Application Areas:Bottle cap｜Home appliance components｜Electrical applications
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | NoBreak | |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 70.0 | J |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | NoBreak | |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 70 | kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak | |
| 23°C | ISO 179/1eU | NoBreak | ||
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 65 | kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ASTM D256 | 770 | J/m |
| 23°C | ASTM D256 | 870 | J/m | |
| -30°C | ISO 180/1A | 60 | kJ/m² | |
| 23°C | ISO 180/1A | 70 | kJ/m² | |
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| UL flame retardant rating | 0.40mm | UL 94 | HB | |
| Burning wire flammability index | 0.8mm | IEC 60695-2-12 | 850 | °C |
| 1.0mm | IEC 60695-2-12 | 960 | °C | |
| Hot filament ignition temperature | 3.0mm | IEC 60695-2-13 | 875 | °C |
| 1.0mm | IEC 60695-2-13 | 875 | °C | |
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| Bending modulus | ISO 178 | 2250 | Mpa | |
| Tensile strain | Break | ISO 527-2/50 | 120 | % |
| Bending modulus | 50.0mmSpan | ASTM D790 | 2230 | Mpa |
| elongation | Break | ASTM D638 | 98 | % |
| Tensile strain | Yield | ISO 527-2/50 | 6.0 | % |
| tensile strength | Break | ISO 527-2/50 | 60.0 | Mpa |
| elongation | Yield | ASTM D638 | 6.0 | % |
| tensile strength | Break | ASTM D638 | 50.3 | Mpa |
| bending strength | Yield,50.0mmSpan | ASTM D790 | 92.4 | Mpa |
| ISO 178 | 85.0 | Mpa | ||
| tensile strength | Yield | ISO 527-2/50 | 57.0 | Mpa |
| Yield | ASTM D638 | 55.5 | Mpa | |
| Tensile modulus | ISO 527-2/1 | 2150 | Mpa | |
| ASTM D638 | 2020 | Mpa | ||
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| RTI Str | UL 746 | 125 | °C | |
| Vicat softening temperature | -- | ISO 306/B120 | 146 | °C |
| Ball Pressure Test | 125°C | IEC 60695-10-2 | Pass | |
| Linear coefficient of thermal expansion | MD：-40to40°C | ASTME831 | 7E-05 | cm/cm/°C |
| MD：23to80°C | ISO 11359-2 | 7.2E-05 | cm/cm/°C | |
| TD：23to80°C | ISO 11359-2 | 7.2E-05 | cm/cm/°C | |
| RTI Elec | UL 746 | 130 | °C | |
| Linear coefficient of thermal expansion | TD：-40to40°C | ASTME831 | 7.5E-05 | cm/cm/°C |
| RTI Imp | UL 746 | 120 | °C | |
| Vicat softening temperature | -- | ISO 306/B50 | 145 | °C |
| Hot deformation temperature | 1.8MPa,Unannealed,3.20mm | ASTM D648 | 124 | °C |
| 1.8MPa,Unannealed,100mmSpan | ISO 75-2/Ae | 128 | °C | |
| 0.45MPa,Unannealed,3.20mm | ASTM D648 | 139 | °C | |
| Vicat softening temperature | ASTM D152510 | 145 | °C | |
| Hot deformation temperature | 0.45MPa,Unannealed,100mmSpan | ISO 75-2/Be | 140 | °C |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| Water absorption rate | Equilibrium,23°C,50%RH | ISO 62 | 0.15 | % |
| density | ASTM D792 | 1.18 | g/cm³ | |
| ISO 1183 | 1.19 | g/cm³ | ||
| Melt Volume Flow Rate (MVR) | 300°C/1.2kg | ISO 1133 | 9.00 | cm3/10min |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 10 | g/10min |
| Shrinkage rate | MD：3.20mm | Internal Method | 0.40-0.80 | % |
| Water absorption rate | Saturation,23°C | ISO 62 | 0.35 | % |
| Shrinkage rate | TD：3.20mm | Internal Method | 0.40-0.80 | % |
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| Dissipation factor | 100Hz | ASTM D150 | 1.2E-03 | |
| Dielectric constant | 1MHz | ASTM D150 | 2.64 | |
| 100Hz | ASTM D150 | 2.68 | ||
| Dielectric strength | 0.800mm,inOil | ASTM D149 | 16 | KV/mm |
| Dissipation factor | 1MHz | ASTM D150 | 9.3E-03 | |
| Volume resistivity | ASTM D257 | >1.0E+15 | ohms·cm | |
| Surface resistivity | ASTM D257 | >1.0E+15 | ohms | |
| hardness | Test Condition | Test Method | Test Result | Test Unit |
| Rockwell hardness | L-Sale | ASTM D785 | 89 | |
| R-Sale | ASTM D785 | 121 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.