PPO NORYL™ EXNL1117BK SABIC INNOVATIVE US

292

Unit Price:US$ 3,910 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High temperature resistance｜Hydrolysis resistance｜wear resistant
Application Areas:Instrument panel components｜Mechanical Engineering｜valve
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Dart impact	23°C,TotalEnergy	ASTM D3763	30.0	J
Impact strength of cantilever beam gap	23°C	ISO 180/1A	9.3	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-30°C	ISO 180/1A	4.6	kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179/1eA	10	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.5mm	UL 94	V-1
UL flame retardant rating	UL flame retardant rating	2.5mm	UL 94	V-0
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Bending modulus		ISO 178	2650	Mpa
bending strength		ISO 178	100	Mpa
bending strength	bending strength	Yield,50.0mmSpan	ASTM D790	100	Mpa
Bending modulus	50.0mmSpan	ASTM D790	2730	Mpa
Tensile strain	Break	ISO 527-2/50	4.4	%
elongation	Break	ASTM D638	5.2	%
Tensile strain	Yield	ISO 527-2/50	3.3	%
elongation	Yield	ASTM D638	3.6	%
tensile strength	Break	ISO 527-2/50	60.0	Mpa
	tensile strength	Break	ASTM D638	55.0	Mpa
		tensile strength	Yield	ISO 527-2/50	65.0	Mpa
		tensile strength	tensile strength	Yield	ASTM D638	67.0	Mpa
Tensile modulus		ISO 527-2/1	2810	Mpa
Tensile modulus	Tensile modulus		ASTM D638	2560	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Vicat softening temperature	--	ISO 306/B50	96.0	°C
Vicat softening temperature	Vicat softening temperature		ASTM D152510	96.0	°C
Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	75.0	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	75.0	°C
Vicat softening temperature	--	ISO 306/B120	98.0	°C
Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	7.7E-05	cm/cm/°C
	Linear coefficient of thermal expansion	MD：-40to40°C	ISO 11359-2	7.7E-05	cm/cm/°C
		Linear coefficient of thermal expansion	TD：-40to40°C	ASTME831	7.9E-05	cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：-40to40°C	ISO 11359-2	7.9E-05	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	9E-03	%
Water absorption rate	Water absorption rate	Saturation,23°C	ISO 62	0.060	%
Shrinkage rate	MD：3.20mm	Internal Method	0.50-0.70	%
Melt Volume Flow Rate (MVR)	280°C/2.16kg	ISO 1133	25.0	cm3/10min
melt mass-flow rate	280°C/2.16kg	ASTM D1238	25	g/10min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Other Prices

Supplier	Unit Price
Dongguan Junlong	US$ 3910 /MT

Supplier Join

Get App

Top

PPO NORYL™ EXNL1117BK SABIC INNOVATIVE US

Material Description

Technical Data Sheet

Other Prices

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index