LCP VECTRA® FIT72 D-2 BK210P CELANESE USA
166
- Unit Price:US$ 6,251 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:50MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Electrostatic discharge protection|Halogen-free|Flame retardant|enhance|Glass fiber reinforced|Low warpage| high flowability| and flame retardancy|Filler: Glass mineral|35% filler by weight
- Application Areas:Fitness equipment|Home appliance components|Automotive Applications
- Color:--
- Grade:--
Technical Data Sheet
thermal performance | Test Condition | Test Method | Test Result |
---|---|---|---|
Heat Deflection Temperature | 1.8 MPa, 未退火 | ISO 75-2/A | 240 °C |
melting temperature | ISO 11357-3 | 331 °C | |
Linear coefficient of thermal expansion | MD | ISO 11359-2 | 8E-06 cm/cm/℃ |
TD | ISO 11359-2 | 4.3E-05 cm/cm/℃ | |
Heat Deflection Temperature | 0.45 MPa, 未退火 | ISO 75-2/B | 284 °C |
Linear coefficient of thermal expansion | MD | ISO 11359-2 | 8E-06 cm/cm/°C |
TD | ISO 11359-2 | 4.3E-05 cm/cm/°C | |
Heat Deflection Temperature | 0.45MPa,未退火 | ISO 75-2/B | 284 °C |
1.8MPa,未退火 | ISO 75-2/A | 240 °C | |
melting temperature | ISO 11357-3 | 331 °C |
Impact resistance | Test Condition | Test Method | Test Result |
---|---|---|---|
Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 30 kJ/m² |
Physical properties | Test Condition | Test Method | Test Result |
---|---|---|---|
shrinkage rate | TD | ISO 294-4 | 0.43 % |
MD | ISO 294-4 | 0.05 % | |
TD | ISO 294-4 | 0.43 % | |
MD | ISO 294-4 | 0.050 % |
mechanical properties | Test Condition | Test Method | Test Result |
---|---|---|---|
Tensile modulus | ISO 527-2/1A/1 | 12000 Mpa | |
tensile strength | 断裂 | ISO 527-2/1A/5 | 110 Mpa |
Tensile strain | 断裂 | ISO 527-2/1A/5 | 2 % |
flexural modulus | 23℃ | ISO 178 | 12000 Mpa |
bending strength | 23℃ | ISO 178 | 140 Mpa |
Fracture bending strain | ISO 178 | 2.5 % | |
Charpy Notched Impact Strength | 23℃ | ISO 179/1eA | 8 kJ/m² |
Impact strength of simply supported beam without notch | 23℃ | ISO 179/1eA | 30 kJ/m² |
Tensile modulus | ISO 527-2/1A/1 | 12000 Mpa | |
tensile strength | 断裂 | ISO 527-2/1A/50 | 110 Mpa |
Tensile strain | 断裂 | ISO 527-2/1A/50 | 2.0 % |
flexural modulus | 23°C | ISO 178 | 12000 Mpa |
bending strength | 23°C | ISO 178 | 140 Mpa |
Fracture bending strain | ISO 178 | 2.5 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.