PC/PBT XENOY™ X4850-78211 SABIC INNOVATIVE US
222
- Unit Price:US$ 3,137 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:113MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High mobility｜High impact resistance｜Dimensional stability
- Application Areas:Automotive Applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ball-indentation hardness | H358/30 | ISO 2039-1 | 105 Mpa |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火,3.20mm | ASTM D648 | 125 °C |
| 0.45MPa,Unannealed,64.0mmSpan | ISO 75-2/Bf | 121 °C | |
| 1.8MPa,未退火,3.20mm | ASTM D648 | 101 °C | |
| 1.8MPa,Unannealed,64.0mmSpan | ISO 75-2/Af | 99.0 °C | |
| vicat | ASTM D152511 | 134 °C | |
| -- | ISO 306/B50 | 133 °C | |
| -- | ISO 306/B120 | 135 °C | |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 5.2E-05 cm/cm/°C |
| MD：-30到80°C | ISO 11359-2 | 6.3E-05 cm/cm/°C | |
| TD：-40到40°C | ASTME831 | 7.5E-05 cm/cm/°C | |
| TD：-30to80°C | ISO 11359-2 | 8.1E-05 cm/cm/°C | |
| thermal conductivity | ISO 8302 | 0.20 W/m/K |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 11 kJ/m² |
| 23°C | ISO 179/1eA | 20 kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak |
| 23°C | ISO 179/1eU | NoBreak | |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 7.0 kJ/m² |
| 0°C | ISO 180/1A | 11 kJ/m² | |
| 23°C | ISO 180/1A | 20 kJ/m² | |
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | NoBreak |
| 23°C | ISO 180/1U | NoBreak | |
| Dart impact | -20°C,TotalEnergy | ASTM D3763 | 60.0 J |
| 23°C,TotalEnergy | ASTM D3763 | 60.0 J | |
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 100 J |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.14 % |
| melt mass-flow rate | 266°C/5.0kg | ASTM D1238 | 4.5 g/10min |
| Melt volume flow rate | 265°C/5.0kg | ISO 1133 | 4.00 cm3/10min |
| shrinkage rate | MD：3.20mm | 内部方法 | 0.70-0.90 % |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.42 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| flexural modulus | ISO 178 | 3500 Mpa | |
| bending strength | ISO 178 | 94.0 Mpa | |
| Yield,50.0mmSpan | ASTM D790 | 99.0 Mpa | |
| Taber abraser | 1000Cycles,1000g,CS-17转轮 | 内部方法 | 30.0 mg |
| Tensile modulus | ASTM D638 | 4000 Mpa | |
| ISO 527-2/1 | 3850 Mpa | ||
| tensile strength | 屈服 | ASTM D638 | 58.0 Mpa |
| 屈服 | ASTM D638 | 65.0 Mpa | |
| 屈服 | ISO 527-2/5 | 58.0 Mpa | |
| 屈服 | ISO 527-2/50 | 63.0 Mpa | |
| 断裂3 | ASTM D638 | 60.0 Mpa | |
| 断裂4 | ASTM D638 | 55.0 Mpa | |
| 断裂 | ISO 527-2/5 | 50.0 Mpa | |
| 断裂 | ISO 527-2/50 | 45.0 Mpa | |
| elongation | 屈服 | ASTM D638 | 3.8 % |
| 屈服 | ASTM D638 | 3.7 % | |
| Tensile strain | 屈服 | ISO 527-2/5 | 3.4 % |
| 屈服 | ISO 527-2/50 | 3.5 % | |
| elongation | 断裂3 | ASTM D638 | 140 % |
| 断裂4 | ASTM D638 | 130 % | |
| Tensile strain | 断裂 | ISO 527-2/5 | 80 % |
| 断裂 | ISO 527-2/50 | 30 % | |
| flexural modulus | 50.0mmSpan | ASTM D790 | 3700 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.