PC LEXAN™ LUX9612 WH8E490X SABIC INNOVATIVE NANSHA
169
- Unit Price:US$ 3,415 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:18MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:optical performance ｜UV resistance｜Weather resistance｜transparent｜Flame retardant
- Application Areas:Lighting applications｜Home appliance components｜Automotive sector
- Color:--
- Grade:Light diffusion level
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 0.45MPa, Unanealed, 64.0mm span | ISO 75-2/Bf | 135 °C | |
| 1.8MPa, Unanealed, 3.20mm | ASTM D648 | 123 °C | |
| 1.8MPa, Unanealed, 64.0mm span | ISO 75-2/Af | 123 °C | |
| vicat | ASTM D152513 | 140 °C | |
| ball-indentation hardness | 125°C | IEC 60695-10-2 | Pass |
| Linear coefficient of thermal expansion | MD:-40到40°C | ASTME831 | 6.8E-05 cm/cm/°C |
| TD:-40到40°C | ASTME831 | 6.7E-05 cm/cm/°C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 1.50mm | UL 94 | V-0 |
| Burning wire flammability index | 1.00mm | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | 1.00mm | IEC 60695-2-13 | 850 °C |
| 1.50mm | IEC 60695-2-13 | 850 °C |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 23°C | ASTM D256 | 400 J/m | |
| ISO 180/1A | 40 kJ/m² | ||
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 70.0 J |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 7.0 g/10min |
| shrinkage rate | MD：3.20mm | 内部方法 | 0.60-0.80 % |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.35 % |
| 平衡,23°C,50%RH | ISO 62 | 0.15 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 3 |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 1 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 3 |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| --1 | ASTM D638 | 2300 Mpa | |
| yield | ASTM D638 | 62.0 Mpa | |
| Yield, 50.0mm span | ASTM D790 | 95.0 Mpa | |
| yield | ISO 527-2/50 | 62.0 Mpa | |
| fracture | ASTM D638 | 65.0 Mpa | |
| ISO 527-2/50 | 58.0 Mpa | ||
| yield | ASTM D638 | 6.0 % | |
| ISO 527-2/50 | 6.0 % | ||
| fracture | ASTM D638 | 80 % | |
| ISO 527-2/50 | 75 % | ||
| 50.0mm span | ASTM D790 | 2160 Mpa | |
| --7 | ISO 178 | 2250 Mpa | |
| --8 | ISO 178 | 95.0 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.