PA6 LNP™ LUBRICOMP™ PX11311 WH9F059 SABIC INNOVATIVE US

384

Unit Price:US$ 5,679 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
75MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Dimensional stability｜Low Specific Gravity
Application Areas:Automotive body panels｜Automotive sector
Color:--
Grade:Impact resistant grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch		ISO 179	5.3to18 kJ/m²
Suspended wall beam without notch impact strength	23°C	ASTM D4812	180 J/m

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.00mm	UL 94	V-0
Burning wire flammability index	2.00mm	IEC 60695-2-12	960 °C
Hot filament ignition temperature	1.00mm	IEC 60695-2-13	775 °C
Hot filament ignition temperature	Hot filament ignition temperature	3.00mm	IEC 60695-2-13	850 °C

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ASTM D638	7240 Mpa
tensile strength	Break	ASTM D638	52.0 Mpa
elongation	Break	ASTM D638	2.0 %
Bending modulus	50.0mmSpan	ASTM D790	9050 Mpa
bending strength	Break,50.0mmSpan	ASTM D790	76.0 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	199 °C
Linear coefficient of thermal expansion	MD:-40to40°C	ASTME831	3.1E-05 cm/cm/°C
	Linear coefficient of thermal expansion	MD:40to120°C	ASTME831	1.9E-05 cm/cm/°C
		Linear coefficient of thermal expansion	TD:-40to40°C	ASTME831	4.6E-05 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD:40to120°C	ASTME831	7E-05 cm/cm/°C
specific heat		ASTMC351	1420 J/kg/°C
--6		ASTM D790/ISO 178	1.2 W/m/K
--7		ASTM D790/ISO 178	2.1 W/m/K
--8		ISO 22007-2	0.99 W/m/K
--9		ISO 22007-2	1.4 W/m/K

Physical properties	Test Condition	Test Method	Test Result
Melt Volume Flow Rate (MVR)	300°C/10.0kg	ISO 1133	49.0 cm3/10min
Shrinkage rate	MD:24hr	ASTM D955	0.33 %
Shrinkage rate	Shrinkage rate	TD:24hr	ASTM D955	0.48 %
23°C,24hr		Internal Method	0.25 %
Balance, 23 ° C, 50% RH		ISO 62	0.040 %

Electrical performance	Test Condition	Test Method	Test Result
Hot wire ignition	HWI	UL 746	PLC 0
Surface resistivity		ASTM D257	>1.0E+15 ohms
Dielectric strength	1.00mm,inOil	ASTM D149	>10 KV/mm
Dielectric constant	1.10GHz	ASTMES7-83	4.74
Dissipation factor	1.10GHz	ASTMES7-83	7.7E-03
Compared to the anti leakage trace index		IEC 60112	PLC 0
High arc combustion index	HAI	UL 746	PLC 0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.