POM TENAC™ 5013A ASAHI JAPAN
216
- Unit Price:US$ 5,135 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High mobility｜Medium viscosity
- Application Areas:Industrial applications｜Automotive Applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Linear coefficient of thermal expansion | TMA法 | 10 | |
| Heat Deflection Temperature | 0.45MPa | ASTM D648 | 172 °C |
| 1.82MPa | ASTM D648 | 136 °C | |
| melt mass-flow rate | ASTM D1238 | 22 g/10min | |
| Heat Deflection Temperature | HDT | ASTM D648/ISO 75 | 136 ℃（℉） |
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 10 mm/mm.℃ | |
| Heat Deflection Temperature | HDT | ASTM D648/ISO 75 | 172 ℃（℉） |
| other | Test Condition | Test Method | Test Result |
|---|---|---|---|
| characteristic | 含UV紫外线吸收剂和其他耐气候助剂 | ||
| 汽车部件 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| shrinkage rate | 垂直方向 | 旭化成法 | 1.8-2.2 % |
| Water absorption rate | ASTM D570 | 0.2 % | |
| shrinkage rate | 平行方向 | 旭化成法 | 1.8-2.2 % |
| density | ASTM D792/ISO 1183 | 1.42 | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 22 g/10min | |
| Water absorption rate | ASTM D570/ISO 62 | 0.2 % | |
| shrinkage rate | ASTM D955 | 1.8-2.2 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | ASTM D638 | 68 Mpa | |
| Elongation at break | ASTM D638 | 45 % | |
| bending strength | ASTM D790 | 101 Mpa | |
| flexural modulus | ASTM D790 | 3040 Mpa | |
| Impact strength of cantilever beam gap | ASTM D256 | 69 J/m | |
| Rockwell hardness | - | ASTM D785 | 94 M |
| - | ASTM D785 | 120 R | |
| wear resistance | ASTM D1044 | 13 | |
| tensile strength | ASTM D638/ISO 527 | 68 kg/cm²(MPa)[Lb/in²] | |
| elongation | ASTM D638/ISO 527 | 45 % | |
| Rockwell hardness | ASTM D785 | 94 | |
| flexural modulus | ASTM D790/ISO 178 | 3040 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 101 kg/cm²(MPa)[Lb/in²] | |
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 69 kg·cm/cm(J/M)ft·lb/in | |
| Elongation at break | ASTM D638/ISO 527 | 45 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.