PC INFINO® NH-3200 NP Samsung Cheil South Korea

165

Unit Price:US$ 2,480 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
20MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Glass fiber reinforced｜Flame retardant
Application Areas:Audio and video equipment｜Laptop｜Electronic and Electrical Applications
Color:--
Grade:Flame retardant grade

Technical Data Sheet

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.75 mm	UL 94	V-0
	UL flame retardant rating	0.830mm	UL 94	V-0
	UL flame retardant rating	UL flame retardant rating	3.0 mm	UL 94	V-0

mechanical properties	Test Condition	Test Method	Test Result
bending strength	--5	ISO 178	150 Mpa
bending strength	bending strength	--4	ASTM D790	150 Mpa
Bending modulus	--5	ISO 178	6000 Mpa
Bending modulus	Bending modulus	--4	ASTM D790	5900 Mpa
elongation	Break	ISO 527-2/5	3.0 %
elongation	elongation	Break3	ASTM D638	3.0 %
tensile strength	Break	ISO 527-2/5	120 Mpa
	tensile strength	Break3	ASTM D638	120 Mpa
		tensile strength	Yield	ISO 527-2/5	120 Mpa
		tensile strength	tensile strength	Yield3	ASTM D638	120 Mpa
Tensile modulus	--	ISO 527-2/5	5000 Mpa
Tensile modulus	Tensile modulus	--3	ASTM D638	4900 Mpa

injection	Test Condition	Test Method	Test Result
Hot air dryer			80 °C
Vacuum drying machine			80 °C
Hot air dryer			3.0 to 4.0 hr
Vacuum drying machine			4.0 to 6.0 hr
Suggested maximum moisture content			0.040 %
Temperature at the rear of the barrel			260 to 270 °C
Temperature in the middle of the barrel			270 to 290 °C
Temperature at the front of the material cylinder			260 to 280 °C
Spray nozzle temperature			270 °C
Mold temperature			60 to 70 °C
Injection pressure			98.1 Mpa
Back pressure			0.981 to 1.96 Mpa
Screw speed			30 to 100 rpm

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm	ISO 75-2/A	97.0 °C
	Hot deformation temperature	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	100 °C
		Hot deformation temperature	0.45 MPa, Unannealed, 4.00 mm	ISO 75-2/B	102 °C
		Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed, 6.40 mm	ASTM D648	105 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	Flow : 2.00 mm	ISO 294-4	0.10 - 0.40 %
	Shrinkage rate	横向Flow : 2.00 mm	ISO 294-4	0.10 - 0.40 %
		Shrinkage rate	Across FlowFlow : 3.20 mm	ASTM D955	0.10 - 0.40 %
		Shrinkage rate	Shrinkage rate	Flow : 3.20 mm	ASTM D955	0.10 - 0.40 %
melt mass-flow rate	300°C/1.2 kg	ASTM D1238	12 g/10 min
melt mass-flow rate	melt mass-flow rate	250°C/5.0 kg	ASTM D1238	19 g/10 min

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R -Sale	ISO 2039-2	120
Rockwell hardness	Rockwell hardness	R-Scale	ASTM D785	120

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.