PC LEXAN™ FXE1112T-BK1C112T SABIC INNOVATIVE NANSHA
152
- Unit Price:US$ 3,497 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:13MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Thermal stability｜Middle flow
- Application Areas:Electrical applications｜Lighting applications｜Automotive Applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,未退火,3.20mm | ASTM D648 | 122 °C |
| 1.8MPa,Unannealed,64.0mmSpan | ISO 75-2/Af | 117 °C | |
| vicat | ASTM D152510 | 139 °C | |
| -- | ISO 306/B50 | 139 °C | |
| -- | ISO 306/B120 | 140 °C | |
| Linear coefficient of thermal expansion | MD：-40到95°C | ASTME831 | 7.5E-05 cm/cm/°C |
| MD：23到80°C | ISO 11359-2 | 7.5E-05 cm/cm/°C | |
| TD：-40to95°C | ASTME831 | 7.6E-05 cm/cm/°C | |
| TD：23to80°C | ISO 11359-2 | 7.6E-05 cm/cm/°C |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak |
| 23°C | ISO 179/1eU | NoBreak | |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 55 kJ/m² |
| 23°C | ISO 180/1A | 65 kJ/m² | |
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | NoBreak |
| 23°C | ISO 180/1U | NoBreak | |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 74.9 J |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 45 kJ/m² |
| 23°C | ISO 179/1eA | 65 kJ/m² |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 19.0 cm3/10min |
| shrinkage rate | MD：3.20mm | 内部方法 | 0.40-0.80 % |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.24 % |
| 平衡,23°C,50%RH | ISO 62 | 0.093 % | |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 20 g/10min |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| elongation | 屈服 | ASTM D638 | 5.7 % |
| Tensile strain | 屈服 | ISO 527-2/50 | 5.4 % |
| elongation | 断裂 | ASTM D638 | 120 % |
| Tensile strain | 断裂 | ISO 527-2/50 | 120 % |
| flexural modulus | 50.0mm跨距 | ASTM D790 | 2250 Mpa |
| ISO 178 | 2150 Mpa | ||
| bending strength | ISO 178 | 89.5 Mpa | |
| 屈服,50.0mm跨距 | ASTM D790 | 94.8 Mpa | |
| Tensile modulus | ASTM D638 | 2260 Mpa | |
| ISO 527-2/1 | 2340 Mpa | ||
| tensile strength | 屈服 | ASTM D638 | 58.6 Mpa |
| 屈服 | ISO 527-2/50 | 57.8 Mpa | |
| 断裂 | ASTM D638 | 57.1 Mpa | |
| 断裂 | ISO 527-2/50 | 56.8 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.