'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PPS FORTRON® 6165A6 SD3002 CELANESE USA
304
- Unit Price:US$ 5,990 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:75MT
- Delivery Terms:FOB
- Port of Loading :Guangzhou port, China
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
+86 ********View
For more details, please contact the supplier!
Material Description
- Material Properties:Glass fiber reinforced｜Flame retardant｜standard｜High temperature resistance｜Filler: Glass mineral｜Filler by weight｜Filler by weight
- Application Areas:Fiber grade｜Pump parts｜Shell｜Electrical/Electronic Applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 20 | kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 6.0 | kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 7.0 | kJ/m² |
| 23°C | ISO 179/1eA | 7.0 | kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 20 | kJ/m² |
| 23°C | ISO 179/1eU | 20 | kJ/m² | |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 6.0 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| UL flame retardant rating | 0.75mm | UL 94 | V-0 | |
| 1.5mm | UL 94 | V-0 | ||
| Basic Performance | Test Condition | Test Method | Test Result | Test Unit |
| Water absorption rate | 23℃ | ISO 62 | 0.02 | % |
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| tensile strength | Break,23°C | ASTM D638 | 114 | Mpa |
| Impact strength of cantilever beam gap | 23℃ | ISO 180/1A | 6 | kJ/m² |
| tensile strength | ISO 527-1 | 130 | Mpa | |
| elongation | Break | ISO 527-1 | 1.2 | % |
| Bending modulus | ISO 178 | 18800 | Mpa | |
| bending strength | ISO 178 | 210 | Mpa | |
| Rockwell hardness | ISO 2039-2 | 100 | M-scale | |
| Tensile modulus | ISO 527-1 | 19000 | Mpa | |
| tensile strength | Break | ISO 527-2/1A/5 | 130 | Mpa |
| elongation | Break,23°C | ASTM D638 | 1.3 | % |
| Tensile strain | Break | ISO 527-2/1A/5 | 1.2 | % |
| Bending modulus | 23°C | ISO 178 | 18800 | Mpa |
| bending strength | ISO 178 | 210 | Mpa | |
| Tensile modulus | ISO 527-2/1A/1 | 19000 | Mpa | |
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| Hot deformation temperature | 1.8MPa,Unannealed | ASTM D648 | 266 | °C |
| 0.45MPa,Annealed | ASTM D648 | 280 | °C | |
| UL flame retardant rating | 0.750mm | UL 94 | V-0 | |
| Hot deformation temperature | 1.80Mpa | ISO 75-1 | 270 | °C |
| 1.8MPa,Unannealed | ISO 75-2/A | 270 | °C | |
| Glass transition temperature | ISO 11357-2 | 90.0 | °C | |
| Melting temperature | ISO 11357-3 | 280 | °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.9E-05 | cm/cm/°C |
| TD | ISO 11359-2 | 2.4E-05 | cm/cm/°C | |
| Hot deformation temperature | 8.0MPa,Unannealed | ISO 75-2/C | 215 | °C |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| Specific volume | ASTM D792 | 0.502 | cm³/g | |
| density | ASTM D792 | 2.00 | g/cm³ | |
| ISO 1183 | 1.95 | g/cm³ | ||
| Shrinkage rate | ISO 2577 | 0.2-0.6 | % | |
| density | ISO 1183 | 1.95 | g/cm³ | |
| Shrinkage rate | MD | ASTM D955 | 0.10-0.20 | % |
| TD | ASTM D955 | 0.30-0.50 | % | |
| TD | ISO 294-4 | 0.30-0.70 | % | |
| SpecificHeatCapacity of Melt | Internal Method | 1600 | J/kg/°C | |
| Water absorption rate | Saturation,23°C | ISO 62 | 0.020 | % |
| Shrinkage rate | MD | ISO 294-4 | 0.20-0.60 | % |
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| Dissipation factor | 1kHz | ASTM D150 | 1E-03 | |
| 1MHz | ASTM D150 | 9E-04 | ||
| 1MHz | IEC 60250 | 2E-03 | ||
| Surface resistivity | IEC 60093 | >1.0E+15 | ohms | |
| Volume resistivity | ASTM D257 | 1E+16 | ohms·cm | |
| IEC 60093 | >1.0E+15 | ohms·cm | ||
| Dielectric strength | IEC 60243-1 | 25 | KV/mm | |
| Dielectric constant | 1kHz | ASTM D150 | 4.50 | |
| 1MHz | ASTM D150 | 4.50 | ||
| Relative permittivity | 1MHz | IEC 60250 | 5.60 | |
| Arc resistance | ASTM D495 | 182 | sec | |
| Compared to the anti leakage trace index | IEC 60112 | PLC 3 | ||
| hardness | Test Condition | Test Method | Test Result | Test Unit |
| Rockwell hardness | M-Scale | ISO 2039-2 | 100 | |
| M-Scale | ASTM D785 | 100 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.